Microstructure and properties of ElectronBeamWeldingJoint for Ti-6321 Large Thickness Titanium Alloy
Author:
Affiliation:

Luoyang Ship Material Reserach Institute

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用真空电子束焊机实现94mm大厚度Ti-6321(名义成分为Ti-6Al-3Nb-2Zr-1Mo)钛合金全厚度焊接。通过在接头根部填加锁底结构形式获得良好成形的焊缝,接头呈钉形焊缝形貌,深宽比约为16。结果表明:焊缝区为粗大柱状晶,内部排列针状α"马氏体相及编织状片层α相;熔合区是柱状晶与等轴晶联生;单侧热影响区宽约2 mm左右。焊缝区和热影响区的硬度值比母材低,焊接接头拉伸强度与母材相当,拉伸试样均断于焊缝区。焊缝区和热影响区都有较好的冲击韧性,焊接接头厚度方向上力学性能的均匀性较好。

    Abstract:

    Vacuum electron beam welding was used to realize the full thickness welding of Ti-6321 (nominal component Ti-6Al-3Nb-2Zr-1Mo)titanium alloy with 94mm large thickness.The full thickness of the welded joint can be well formed with the method of bottom locking at the bottom. The welded joint shows approximately parallel weld morphology, and the depth width ratio is about 16.The results show that the weld center is composed of coarse columnar crystal and internally staggered acicular α and α" phase.The transition from coarse grain to fine grain near the fusion zone. The width of unilateral heat affected zone is about 2 mm. The microhardness of the weld zone and the heat affected zone were both lower than that of base metal.The tensile strength of welded joint was equivalent to that of the base metal, and the fracture occured in the weld metal.Both the weld zone and the heat affected zone have better impact toughness.The strength and toughness of the welded joint are excellent.The mechanical properties in the direction of welded joint have good uniformity.

    参考文献
    相似文献
    引证文献
引用本文

高奇. Ti-6321钛合金电子束焊接接头组织及性能[J].稀有金属材料与工程,2020,49(3):990~996.[Gaoqi. Microstructure and properties of ElectronBeamWeldingJoint for Ti-6321 Large Thickness Titanium Alloy[J]. Rare Metal Materials and Engineering,2020,49(3):990~996.]
DOI:10.12442/j. issn.1002-185X.17Ti2019167

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-01-29
  • 最后修改日期:2019-09-03
  • 录用日期:2019-09-04
  • 在线发布日期: 2020-04-08
  • 出版日期: