Structures and Properties of MoLa Alloy Wire
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    研究了粉末冶金和压力加工方法制取的φ0.6mmMoLa丝退火前后的显微组织,抗拉强度,延伸率,弯折次数等,并与同规格Mo;丝进行了对比,结果表明,MoLa丝的再结晶温度达1800℃,比Mo,丝高600℃以上,完全再结晶后形成燕尾搭接状组织。经高温退火和再结晶退火后其抗拉强度,塑性,韧性都明显优于Mo1丝。

    Abstract:

    Microstructures, tensile strength, elongation and flexibility before and after annealing have been studied for 06 mm diameter MoLa wire made by powder metallurgy and pressure working, as compared with the same size of Mo1 wire. The results show that the recrystalling temperature of MoLa wire is 1 800, which is 600 higher than that of Mo1 wire. After complete recrystallization, MoLa wire has an interlocking grain structure. The tensile strength, plasticity and tonghness of MoLa wire is higher than those of Mo1 wire after high temperature annealing and/or recrystallization annealing.

    参考文献
    相似文献
    引证文献
引用本文

李淑霞 魏光明.钼镧合金丝的组织及性能[J].稀有金属材料与工程,1999,(3):186~188.[Li Shuxia, Wei Guangming, Wang Siqing. Structures and Properties of MoLa Alloy Wire[J]. Rare Metal Materials and Engineering,1999,(3):186~188.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: