Effect of Hydrogen on Fracture Activation Energy of Metallic Materials
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    研究了两种低碳锰钢在空气和H2S腐蚀介质条件下断裂寿命与应力温度的关系,并从断裂激活能的角度分析了氢的影响。结果表明:氢的存在使断裂激活能约降低74%。这说明其减弱了原子间键合力。

    Abstract:

    The relation of fracture lifetime to stress and temperature has been investigated for two low carbon manganese steels in air and H 2S, The influence of hydrogen on the fracture activation energy is studied. The results show that hydrogen reduces the fracture activation energy by 74%, that is, atomic binding force decreases.

    参考文献
    相似文献
    引证文献
引用本文

张旺峰 朱金华.氢对金属材料断裂激活能的影响[J].稀有金属材料与工程,1999,(4):225~227.[Zhang Wangfeng, Zhu Jinhua. Effect of Hydrogen on Fracture Activation Energy of Metallic Materials[J]. Rare Metal Materials and Engineering,1999,(4):225~227.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: