SEM In-Situ Observation on Crack Initiation and Propagation induced by Inclusion in PM Rene95
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    通过SEM原位拉伸试验观察了P/M Rene 95合金中的非金属夹杂在拉伸状态下导致裂纹萌生、扩展的微观力学行为,结果表明:在原位拉伸过程中,裂纹首先在试样表面的夹杂物处产生,裂纹主要萌生于夹杂物/合金基体的界面;随着外加应力的增加;裂纹极易沿夹杂物/基体界面扩展,向基体深入;最后,部分夹杂与基体完全分离、脱落,一些夹杂物的材料制备过程中被破碎成若干碎片,增加了裂纹萌生的几率。

    Abstract:

    The crack initiation and propagation in Al2O3 seeded P/M Rene95 have been studied by SEM observation in-situ for tension loading stage of the P/M Rene95 sample. The results show that during SEM in-situ tension process, cracks initiate at ceramic inclusions. Generally, the cracks nucleate at the inclusion/matrix interface, and easily propagate along the interfaces and reach the matrix. At last, some inclusion particles may separate from the matrix and fall off.

    参考文献
    相似文献
    引证文献
引用本文

张丽娜,张麦仓,等. Ni基P/M Rene 95合金中非金属夹杂物导致裂纹萌生和扩展的扫描电镜原位观察[J].稀有金属材料与工程,2001,(2):123~126.[Zhang Lina, Zhang Maicang, Li Xao, Dong Jianxin, Xie Xishan. SEM In-Situ Observation on Crack Initiation and Propagation induced by Inclusion in PM Rene95[J]. Rare Metal Materials and Engineering,2001,(2):123~126.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:2000-09-04
  • 录用日期:
  • 在线发布日期:
  • 出版日期: