Research on Corrosion-Resistance of Rapidly Solidified Aluminum Alloys
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用腐蚀失重法和极化曲线,对比研究了FVS0611,FVS0812,2618,2618 Sc,2014,6061合金在人工模拟海水和海洋环境中的耐蚀性能。结果表明:2014,2618和2618 Sc腐蚀较严重;RS/PM生产的FVS0611,FVS0812和6061有较小的腐蚀速率,出现明显的钝化现象;并因为加工残余应力导致出现钝化-腐蚀-再钝化现象。

    Abstract:

    Through corrosion weight-losing and polarization curve test, the corrosion-resistance properties of FVS0611, FVS0812, 6061, 2618, 2618+Sc, 2014 alloys under artificial seawater and oceanic condition have been investigated. It shows that FVS0611, FVS0812 and 6061 alloys prepared by RS/PM have a low corrosion while 2618, 2618+Sc and 2014 alloys has high corrosion. FVS0611, FVS0812 and 6061 alloys have obvious passivation. In the meantime, a phenomenon of passivation-corrosion-passivation occurs among them because residual process stress exists

    参考文献
    相似文献
    引证文献
引用本文

周涛 黄伯云 周科朝 黎文献.快速凝固耐热铝合金耐蚀性能的研究[J].稀有金属材料与工程,2004,33(2):187~189.[Zhou Tao, Huang Boyun, Zhou Kechao, Li Wenxian. Research on Corrosion-Resistance of Rapidly Solidified Aluminum Alloys[J]. Rare Metal Materials and Engineering,2004,33(2):187~189.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:2002-07-08
  • 录用日期:
  • 在线发布日期:
  • 出版日期: