    摘要:

    通过Gleeble-1500热模拟机研究丁庄特高温度下工业纯铁的氧化行为。结果表明,随着氧化温度的升高和保温时间的延长,氧化增重持续增加;特高温氧化产生了多层氧化膜,氧通过破损的外层氧化膜通道向较致密的内层氧化膜扩敬及向金属基体渗透,实现了工业纯钛的整个特高温氧化过程。

    Abstract:

    The extreme high temperature oxidation behavior of commercial pure titanium was researched by Gleeble-1500 thermal simulator. The results show that the weight gain increase continually with the increase of the oxidation temperature and the time of holding temperature. There are several oxide layers at extreme high temperature. Oxygen diffuses from the path in the cracked outer oxide layer into rather compact inner oxide layer and further into metal, which actualize the commercial pure titanium's oxidation at extreme high temperature.

    参考文献
    相似文献
    引证文献
引用本文

金泰来 魏建锋 顾兆林 赵永庆 常辉.工业纯钛在特高温度下的氧化行为研究[J].稀有金属材料与工程,2005,34(12):1998~2001.[Jin Tailai, Wei Jianfeng, Gu Zhaolin, Zhao Yongqing, Chang Hui. Research on Extreme High Temperature Oxidation Behavior of Commercial Pure Titanium[J]. Rare Metal Materials and Engineering,2005,34(12):1998~2001.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2004-07-29
  • 最后修改日期:2005-10-11
  • 录用日期:
  • 在线发布日期:
  • 出版日期: