Study on the Insertion Behaviors of Lithium-Ions into Bi2Te3/Polyaniline Composites Electrodes
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用机械共混法制备了复合材料Bi2Te3/PAn,并对其电化学嵌锂性能进行了研究.研究发现Bi2Te3/PAn快速充放电性能良好,在以100 mA·g-1的电流密度充放电时首次可逆容量为480 mAh·g-1,到第20个循环时容量保持在200mAh·g-1.通过非原位X射线衍射方法研究其嵌锂机理,发现Bi2Te3在首次放电时分解,在随后的循环中以Te和Bi为嵌锂中心进行可逆储锂.

    Abstract:

    Bi2Te3/polyaniline composites were prepared by mechanical blending and the electrochemical properties were studied with lithium anode model cell Li|LiPF6(EC+DMC) |Bi2Te3/PAn. A reversible capacity of about 480mAhg-1 has been obtained in the first cycle. The reversible capacity keeps about 200 mAhg-1 in the first 20 cycles. The mechanism of lithium insertion into Bi2Te3/PAn was analyzed by ex situ XRD.

    参考文献
    相似文献
    引证文献
引用本文

张丽娟 赵新兵 刘欣艳 夏定国 胡淑红.无机有机复合材料Bi2Te3/PAn电化学嵌锂性能研究[J].稀有金属材料与工程,2005,34(4):605~608.[Zhang Lijuan, Zhao Xinbing, Liu Xinyan, Xia Dingguo, Hu Shuhong. Study on the Insertion Behaviors of Lithium-Ions into Bi2Te3/Polyaniline Composites Electrodes[J]. Rare Metal Materials and Engineering,2005,34(4):605~608.]