Effect of Carbon Nanotubes on Electrochemical Properties of LaNi5 Alloy
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用LaNi5稀土合金作为催化剂,用化学气相沉积法(CVD)制备了碳纳米管。研究了含有5%碳纳米管的LaNi5稀土合金电极样品的电化学性能。测定了碳纳米管电极的电化学储氢性能。实验发现:含有碳纳米管的LaNi5稀土合金的电化学放电容量更高,当放电电流密度为100mA/g时,其电化学储氢量高达385mAh/g。其循环寿命也得到了较大改善。循环100次,放电容量仅下降15%。

    Abstract:

    The electrochemical properties of doped 5% carbon nanotubes(CNTs) LaNi5 electrode have been investigated. The CNTs were synthesized by chemical vapor deposition method (CVD) using lanthanum nickel alloy(LaNi5) as the catalyst. Three-electrode system was introduced to test the electrochemical hydrogen storage behaviors of CNTs with Ni(OH)2/NiOOH as the assistant electrode and Hg/HgO as the reference electrode. 6mol/L KOH was used as the electrolyte, and the high discharge capacity was measured of 385 mAh/g at a discharge current of 100 mA/g. The doped 5% CNTs LaNi5 electrodes showed higher electrochemical hydrogen storage capacities and a longer cycle life than those of the un-droped CNTs. In addition, the discharge capacity decay was only 15% after 100 cycles.

    参考文献
    相似文献
    引证文献
引用本文

易双萍 付小娟 朱燕娟 陈易明 张海燕 刘平波.碳纳米管对LaNi5稀土合金电化学性能的影响[J].稀有金属材料与工程,2005,34(4):609~611.[Yi Shuangping, Fu Xiaojuan, Zhu Yanjuan, Chen Yiming, Zhang Haiyan, Liu Pingbo. Effect of Carbon Nanotubes on Electrochemical Properties of LaNi5 Alloy[J]. Rare Metal Materials and Engineering,2005,34(4):609~611.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:2003-07-21
  • 录用日期:
  • 在线发布日期:
  • 出版日期: