Mechanism of CREM Process on Restraining Macro-Segregation of Solute Elements in 7075 Aluminum Alloy Ingot by DC Cast
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    实验研究了CREM法半连铸7075铝合金过程中,低频交变电磁场对凝固前沿形态、微观组织结构、非平衡凝固液固相线位置、结晶区间间隔以及温度场和流动场的影响规律。并据此对CREM法抑制7075铝合金半连铸坯中溶质元素宏观偏析的机理进行了分析和说明。

    Abstract:

    In the producing process of 7075 aluminum alloy by CREM method, the effects of electromagnetic field with low frequency on the evolution of solidifying front shape, non-dendritic structure, liquidus and solidus temperature of non-equilibrium freezing, solidification interval, flow pattern and temperature field have been experimentally investigated. An explanation is also given to the mechanism of CREM process on restraining macro-segregation of solute elements in 7075 aluminum alloy ingot by DC cast.

    参考文献
    相似文献
    引证文献
引用本文

张勤 崔建忠. CREM法抑制7075铝合金半连铸坯中溶质元素宏观偏析的机制[J].稀有金属材料与工程,2005,34(4):627~631.[Zhang Qin, Cui Jianzhong. Mechanism of CREM Process on Restraining Macro-Segregation of Solute Elements in 7075 Aluminum Alloy Ingot by DC Cast[J]. Rare Metal Materials and Engineering,2005,34(4):627~631.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:2003-09-22
  • 录用日期:
  • 在线发布日期:
  • 出版日期: