Preparation of Monodispersed Spherical Y2O3:Eu3+ Nanocrystalline
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用凝胶网格共沉淀法,以明胶为反应基质制备了单分散球形纳米Y2O3:Eu^3 荧光粉,考察了制备条件对产物粒径的影响。利用X射线衍射(XRD)、透射电子显微镜(TEM)和荧光光谱等手段对样品进行了表征。结果表明:该法制得产物为球形,一次晶粒粒径在13nm~25am之间,且粒度分布均匀,与微米晶相比,该纳米晶的激发光谱发生明显红移。

    Abstract:

    Monodispersed spherical Y2O3:Eu3+ nanocrystallines were successfully prepared by a novel gel-network coprecipitition process. The effect of reaction conditions on the resulting particles was investigated. XRD,TEM and fluoresce spectra were used to characterize the samples. The results show that the samples were spherical with a particle size of 13 nm-25 nm. Compared with micronscale Y2O3:Eu3+, a clear red shift occurs in the excitation spectrum of Y2O3:Eu3+ nanocrystalline prepared by the present work.

    参考文献
    相似文献
    引证文献
引用本文

周建国 李振泉 赵凤英 夏树屏 高世扬.均分散球形Y2O3:Eu^3+纳米晶的制备[J].稀有金属材料与工程,2005,34(6):932~935.[Zhou Jianguo, Li Zhenquan, Zhao Fengying, Xia Shuping, Gao Shiyang. Preparation of Monodispersed Spherical Y2O3:Eu3+ Nanocrystalline[J]. Rare Metal Materials and Engineering,2005,34(6):932~935.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:2003-07-28
  • 录用日期:
  • 在线发布日期:
  • 出版日期: