Determination of the Isothermal Section of Ni-Cr-Mo Ternary System at 1358 K
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    应用三元扩散偶技术测定了Ni-Cr-Mo三元系1358 K的等温截面,借助电子探针微区成分分析方法分析了Ni-Cr-Mo三元扩散偶的相区成分,并对其相关系进行了研究.测得Ni-Cr-Mo三元扩散偶在1358 K下存在一个中间化合物NiMo,Cr和Mo在扩散偶中形成连续固溶体,Ni和(Cr,Mo)有限固溶,扩散偶中未发现三元中间化合物.实验发现Ni-Cr-Mo三元系1358 K的等温截面存在一个三相区:Ni+NiMo+(Cr,Mo).

    Abstract:

    The isothermal section of Ni-Cr-Mo ternary system at 1358 K was determined by means of diffusion triple and electron microprobe analysis. The results indicate that one binary intermetallic of NiMo is formed in Ni-Cr-Mo ternary system at 1358 K. In this diffusion triple, Cr and Mo formed into a continuous solid solution, and Ni and (Cr,Mo) formed into a finite solid solution. No ternary compound was observed. One three-phase region of Ni+NiMo+(Cr, Mo) exixts in the isothermal section of Ni-Cr-Mo ternary system at 1358 K.

    参考文献
    相似文献
    引证文献
引用本文

王日初,冯艳,毕豫,金展鹏. Ni-Cr-Mo三元系1358 K等温截面的测定[J].稀有金属材料与工程,2005,34(9):1369~1372.[Wang Richu, Feng Yan, Bi Yu, Jin Zhanpeng. Determination of the Isothermal Section of Ni-Cr-Mo Ternary System at 1358 K[J]. Rare Metal Materials and Engineering,2005,34(9):1369~1372.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:2004-04-16
  • 录用日期:
  • 在线发布日期:
  • 出版日期: