Low Cycle Fatigue Behavior of Ti-1023 Titanium Alloy at Room Temperature
  • 摘要
  • | |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • | |
  • 文章评论
    摘要:

    研究了室温Ti-1023钛合金由应变控制的低周疲劳行为。对循环应力-应变数据和应变-疲劳寿命数据进行了分析,通过双对数线性回归处理,得出了Coffin-Mason处理模型的疲劳参数。结果表明:合金总应变幅在0.6%-0.8%时,循环初期表现出轻微的循环硬化,然后循环稳定;总应变幅超过0.8%时则表现为循环软化。表明合金的循环应力响应行为取决于外加总应变幅。

    Abstract:

    Low cyclic fatigue behavior of Ti-1023 titanium alloy has been investigated under a fully reversed total strain-controlled mode. The strain-life and cyclic stress-strain data were analyzed to determine the individual strain fatigue parameters. It is found that the Ti-1023 alloy exhibited an initial slight cyclic hardening, followed by stable cycle at a total strain amplitude of 0.6%-0.8%, then cyclic softening at a total strain amplitude of above 0.8% to 3.0%. It is considered that the cyclic stress response behavior of Ti-1023 alloy depends on the total strain amplitude.

    参考文献
    相似文献
    引证文献
引用本文

黄利军 黄旭. Ti-1023钛合金的低周疲劳行为[J].稀有金属材料与工程,2006,35(5):703~706.[Huang Lijun, Huang Xu. Low Cycle Fatigue Behavior of Ti-1023 Titanium Alloy at Room Temperature[J]. Rare Metal Materials and Engineering,2006,35(5):703~706.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2005-03-08
  • 最后修改日期:2005-03-08