VFe合金取代TiCr1.8合金中部分Cr对其结构和储氢性能的影响

Influences of Partial Substitution of VFe Alloys for Cr on Structure and Hydrogen Storage Performances of TiCr1.8 Alloy

摘要:

采用XRD、PCT和TG-DSC方法研究了VFe合金取代TiCr1.8合金中部分Cr对其结构与吸放氢性能的影响.结果表明:随VFe取代Cr的量的增加,合金的相组成逐步由Laves相转变为BCC相,而且BCC相的晶胞参数随合金中VFe含量的增加而增大;合金的最大储氢量随VFe含量的增加而升高,合金的最大储氢量可达到5.2/结构单元,质量比约3.4%;但合金的可逆储氢量却随合金中VFe含量的增加先升高后降低;氢在BCC相的TiCr1.2(VFe)0.6合金中有两种具有不同结合能的储存位置.

关键词:TiCr基储氢合金;XRD;可逆储氢量;TG-DSC;TiCr based hydrogen storage alloys;XRD;reversible hydrogen storage capacity;TG-DSC;合金;结构;储氢性能;影响;Performances;Hydrogen Storage;Structure;Alloys;Substitution;Partial;Influences;exist;different;energy;decrease;reversible;mass;means;ratio;number

Abstract:

Key words:TiCr基储氢合金;XRD;可逆储氢量;TG-DSC;TiCr based hydrogen storage alloys;XRD;reversible hydrogen storage capacity;TG-DSC;合金;结构;储氢性能;影响;Performances;Hydrogen Storage;Structure;Alloys;Substitution;Partial;Influences;exist;different;energy;decrease;reversible;mass;means;ratio;number