Globularization Mechanisms during Hot Deformation Processes of TC11 Alloy with Lamellar Structure
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用TEM、SEM和EBSD等组织分析技术研究了β退火态片层组织TC11钛合金两相区热变形球化过程中组织的精细结构和晶界特征。结果表明,片层组织的球化过程包括α片内小角度晶界形变和回复亚结构的形成、β相沿亚晶界扩散和晶界滑动作用下片层的解体以及晶界扩散和滑动驱动下α晶粒的球化和组织的均匀化。EBSD测试结果揭示了片层组织两相区热变形的球化机制为α相的连续动态再结晶和β相的动态回复或不连续动态再结晶过程

    Abstract:

    Microstructure and grain boundary character during hot deformation globularization processes of TC11 alloy with annealed-lamellar structure were investigated by TEM, SEM and EBSD techniques. The results indicate that globularization processes include: 1) forming of sub-structures with low-angle boundaries by deformation and recovery in α plates; 2) disintegrating of α plates by diffusion and slipping along grain boundaries; 3) globularizing of α grains and homogenizing of structure by diffusing and slipping along grain boundaries. EBSD testing results indicate that globularization mechanisms during hot deformation processes of the alloy with lamellar structure are continuous dynamic recrystallization occurring in α plates and dynamic recovery or discontinuous dynamic recrystallization occurring in β phase

    参考文献
    相似文献
    引证文献
引用本文

陈慧琴,曹春晓,郭 灵,林 海. TC11钛合金片层组织热变形球化机制[J].稀有金属材料与工程,2009,38(3):421~425.[Chen Huiqin, Cao Chunxiao, Guo Ling, Lin Hai. Globularization Mechanisms during Hot Deformation Processes of TC11 Alloy with Lamellar Structure[J]. Rare Metal Materials and Engineering,2009,38(3):421~425.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2008-02-28
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: