Effects of Nd3+ on Adhesion And Corrosion Resistance of Electroless Ni-P Coating on Sintered Nd-Fe-B Magnets
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    在化学镀液中添加Nd3+,研究其浓度对Ni-P镀层与烧结Nd-Fe-B磁体的结合力和施镀后磁体耐蚀性的影响。测定添加不同浓度Nd3+镀液中所得Ni-P镀层与磁体的结合力,以及镀层在3.5% NaCl(质量分数,下同)溶液中的极化曲线,并结合中性盐雾实验表征施镀后磁体耐蚀性。结果表明,添加2.5 g·L-1 Nd3+时,Ni-P镀层与Nd-Fe-B磁体的结合力从6.4 MPa提高至25.2 MPa;施镀后磁体的自腐蚀电位从–0.382 V升高到–0.148 V,自腐蚀电流密度从4.52 μA·cm-2降低到

    Abstract:

    Ni-P coatings were deposited on sintered Nd-Fe-B magnets through the addition of Nd3+ in the electroless plating solution. The effects of Nd3+ concentration on the adhesion and corrosion resistance of the coatings were investigated. The adhesions between the magnets and the Ni-P coatings were measured in different Nd+ concentration plating solutions, and the polarization curves of the coatings in 3.5% (mass fraction) NaCl solution were plotted, the magnet corrosion resistances were characterized by neutral salt spray experiment. The results showed that the addition of Nd3+ could significantly improve the adhesion and corrosion resistance of Ni-P coatings on magnets. When increasing Nd3+ up to 2.5 g·L-1, the adhesion strength of the Ni-P coating to Nd-Fe-B magnet was enhanced from 6.4 to 25.2 MPa. Synchronously, the corrosion potential Ecorr of the coated magnets in 3.5% NaCl solution increased from -0.382 to -0.148 V, the corrosion current density Icorr decreased from 4.52 to 0.07 μA·cm-2, and the coated magnets could be as long as 256 h free of corrosion in the neutral salt spray, reflecting the improvement of corrosion resistance.

    参考文献
    相似文献
    引证文献
引用本文

吴元騄,罗 伟,严 密. Nd3+对烧结Nd-Fe-B化学镀Ni-P合金结合力和耐蚀性的影响[J].稀有金属材料与工程,2009,38(6):1096~1099.[Wu Yuanlu, Luo Wei, Yan Mi. Effects of Nd3+ on Adhesion And Corrosion Resistance of Electroless Ni-P Coating on Sintered Nd-Fe-B Magnets[J]. Rare Metal Materials and Engineering,2009,38(6):1096~1099.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2008-06-23
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: