TiNbZr合金在热处理过程中的微观组织和力学性能
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

基金项目:


Characterization of Microstructure and Mechanical Properties of TiNbZr Alloy during Heat Treatment
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    TiNbZr合金由真空自耗电弧炉熔炼。研究了固溶,时效处理对该合金的微观组织和力学性能的影响。结果显示,当合金固溶处理1 h后在300和350 oC时效处理时,合金的抗拉强度高达1000 MPa。当固溶后的合金在400和450 oC时效处理时,出现α相。时效时间对α相的析出有重要的作用。当合金在400 oC时效处理9 h后,抗拉强度为850 MPa,延伸率也保持在11%左右

    Abstract:

    TiNbZr alloy was prepared by vacuum consumable arc melting furnace. The effects of solution and aging heat treatment on the microstructure and mechanical properties of this alloy were studied. The results show that ultimate tensile strength over 1000 MPa can be obtained when the alloy is solutioned for 1 h and then aged at 300 and 350 oC. α phase precipitation appears under the condition of the treatment of solution for 1 h, followed by aging at 400 oC and 450 oC. The aging time plays an important part in α phase precipitation. The ultimate tensile strength increases to 850 MPa and the elongation keeps around 11% when the alloy is aged at 400 ℃ for 9 h

    参考文献
    相似文献
    引证文献
引用本文

王立强,杨冠军,杨华斌,曹继敏,吕维洁,张 荻. TiNbZr合金在热处理过程中的微观组织和力学性能[J].稀有金属材料与工程,2009,38(7):1136~1140.[Wang Liqiang, Yang Guanjun, Yang Huabin, Cao Jimin, Lü Weijie, Zhang Di. Characterization of Microstructure and Mechanical Properties of TiNbZr Alloy during Heat Treatment[J]. Rare Metal Materials and Engineering,2009,38(7):1136~1140.]