Effects of Nd on Microstructures and Mechanical Properties of AM60 Magnesium Alloy in Vacuum Melting
Author:
Affiliation:

Fund Project:

National Natural Science Foundation of China(90306014, 20471041)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    研究了稀土Nd对AM60镁合金组织的影响,并分析析出相及其对合金力学性能的影响。结果表明,在AM60合金中加入稀土Nd元素能有效地细化合金组织,使Mg17Al12相分离变细;Nd元素优先与合金中的Al元素反应生成二元高熔点Al11Nd3相;适量的稀土Nd能有效提高合金的抗拉强度、屈服强度和延伸率;过量的稀土Nd则会消耗合金中更多的Al元素和导致Al11Nd3相粗化,使合金的力学性能下降;力学性能测试结果表明,AM60-0.9Nd具有最高的抗拉强度(230 MPa)、最高的屈服强度(127 MPa)和最高延

    Abstract:

    The microstructure changes brought by the addition of Nd element to AM60 magnesium alloy were studied, the precipitating phases were identified and their influences on the mechanical properties of alloys were investigated. Results show that Nd addition makes the refinement of microstructure of the AM60 alloy, and decreases the size of Mg17Al12 phase. Nd element takes a priority to react with Al element over Mg, Mn and Zn forming binary phase Al11Nd3 with high melting point. Certain content of Nd can increase tensile strength, yield strength and elongation of the alloy. But with too much addition, Nd would combine with more Al in matrix and decrease strengthening effect because Al11Nd3 phase would become coarsening. The mechanical property tests indicate that AM60-0.9Nd alloy has the best properties. Maximum tensile strength, maximum yield strength, maximum elongation are 230 MPa, 127 MPa and 14% respectively, increased by 28%, 48% and 250% respectively

    参考文献
    相似文献
    引证文献
引用本文

张金旺,王社斌,张俊远,张金玲,许并社.真空条件下Nd对AM60镁合金组织与性能的影响[J].稀有金属材料与工程,2009,38(7):1141~1145.[Zhang Jinwang, Wang Shebin, Zhang Junyuan, Zhang Jinling, Xu Bingshe. Effects of Nd on Microstructures and Mechanical Properties of AM60 Magnesium Alloy in Vacuum Melting[J]. Rare Metal Materials and Engineering,2009,38(7):1141~1145.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2008-06-16
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: