Coupled Dense Nanocomposite (NdDy)11.5(FeCoNb)82.4B6.1 Bulk Magnets Prepared by SPS
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    使用放电等离子烧结(SPS)制备致密的纳米晶交换耦合Nd2Fe14B/α-Fe永磁合金。研究烧结温度、时间、压力对合金磁性能和显微组织的影响。结果表明,随温度、压力的升高,密度增大,磁能积增加;但温度过高或时间过长,使得晶粒长大,导致矫顽力降低。在烧结压力为500 MPa,烧结温度为700 ℃保温3 min后,得到密度为7.6 g/cm3,晶粒细小的致密块体,其磁性能为:Br=0.81 T,Hci =856 kA·m-1,(BH)m =106 kJ·m-3,其晶粒大小约20 nm。

    Abstract:

    The exchange coupled dense nanocomposite Nd2Fe14B/α-Fe isotropic bulk magnets were prepared by Spark Plasma Sintering (SPS) method. Influence of sintering temperature, time and pressure on the magnetic properties and microstructure was investigated. It is found that the density and magnetic energy product increased with the sintering temperature and pressure increasing; but the coercivity decreased with the temperature or time further increasing. After sintered at 700 ℃, 500 MPa, and held for 3 min, dense bulk magnets with fine grains of about 20 nm were achieved, whose magnetic properties were: Br=0.81T , Hci =856 kA·m-1, (BH)m =106 kJ·m-3; the density was 7.6 g/cm3.

    参考文献
    相似文献
    引证文献
引用本文

马毅龙,刘 颖,李 军,杜慧龙,高 静,高升吉.放电等离子烧结制备纳米晶双相耦合(NdDy)11.5(FeCoNb)82.4B6.1致密磁体[J].稀有金属材料与工程,2009,38(12):2246~2249.[Ma Yilong, Liu Ying, Li Jun, Du Huilong, Gao Jing, Gao Shengji. Coupled Dense Nanocomposite (NdDy)11.5(FeCoNb)82.4B6.1 Bulk Magnets Prepared by SPS[J]. Rare Metal Materials and Engineering,2009,38(12):2246~2249.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2008-11-27
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: