Combustion Synthesis and Photoluminescence of Y2Zr2O7:Tb3+ Nano-Phosphors
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以甘氨酸作燃烧剂采用燃烧法制备Y2Zr2O7:Tb3+纳米晶粉末。用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计对Y2Zr2O7:Tb3+纳米晶的相结构、形貌和发光性质进行研究。结果表明:所得到的纳米晶粒度均匀、结晶完好,属于立方萤石结构。发光光谱的测试表明:Tb3+呈现其特征绿色发射,最强峰位于542 nm处。Tb3+的掺杂摩尔浓度在0.5%~6%的范围内,3%为最佳掺杂浓度。

    Abstract:

    Y2Zr2O7:Tb3+ nano-phosphors were fabricated by combustion synthesis method using glycine as incendiary agent. X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM) and fluorescence spectrometer were used to characterize the phase structure, surface morphology and luminescence property of Y2Zr2O7:Tb3+ nano-phosphors. The results show that the prepared samples have uniform crystallinity and fine crystalline, with a cubic fluorite structure. Typical Tb3+ emission peaks were observed in the fluorescence spectra and the strongest emission at about 542 nm with green color corresponded to the 5D4--→7F5 transition. The doping concentration of Tb3+ was in the range of 0.5%-6%, with the optimum of 3%.

    参考文献
    相似文献
    引证文献
引用本文

王庆凯,王殿元,郭艳艳,吴杏华,常章用,罗江龙.燃烧法制备Y2Zr2O7:Tb3+纳米晶及其发光性质研究[J].稀有金属材料与工程,2009,38(12):2250~2252.[Wang Qingkai, Wang Dianyuan, Guo Yanyan, Wu Xinghua, Chang Zhangyong, Luo Jianglong. Combustion Synthesis and Photoluminescence of Y2Zr2O7:Tb3+ Nano-Phosphors[J]. Rare Metal Materials and Engineering,2009,38(12):2250~2252.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2008-11-27
  • 最后修改日期:2009-09-14
  • 录用日期:
  • 在线发布日期:
  • 出版日期: