TaSi2 Oxidation Protective Coating for SiC Coated Carbon/Carbon Composites
Author:
Affiliation:

Fund Project:

Open (Director) Fund of Shenzhen Key Laboratory of Special Functional Materials of Shenzhen University (0703)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    In order to improve the oxidation protective property of carbon/carbon composites at high temperature, TaSi2 coating was prepared on the surface of SiC coated carbon/carbon composites by pack cementation technique. The crystal structure and morphology of the as-obtained coating was analyzed by XRD and SEM with EDS. The isothermal oxidation test was carried out in air at 1773 K. The results show that the as-prepared coating is composed of SiC, Si and TaSi2. The multilayer coating is about 200 μm in thickness, and there are no cracks in it. The results of EDS indicate that TaSi2 can effectively fill the holes of SiC coating. There is no visible interface between the TaSi2 outer coating and the SiC inner coating. The isothermal oxidation curve of the TaSi2/SiC coated carbon/carbon composites reveals that the coating can effectively protect carbon/carbon composites for 233 h at 1773 K

    Abstract:

    In order to improve the oxidation protective property of carbon/carbon composites at high temperature, TaSi2 coating was prepared on the surface of SiC coated carbon/carbon composites by pack cementation technique. The crystal structure and morphology of the as-obtained coating was analyzed by XRD and SEM with EDS. The isothermal oxidation test was carried out in air at 1773 K. The results show that the as-prepared coating is composed of SiC, Si and TaSi2. The multilayer coating is about 200 μm in thickness, and there are no cracks in it. The results of EDS indicate that TaSi2 can effectively fill the holes of SiC coating. There is no visible interface between the TaSi2 outer coating and the SiC inner coating. The isothermal oxidation curve of the TaSi2/SiC coated carbon/carbon composites reveals that the coating can effectively protect carbon/carbon composites for 233 h at 1773 K

    参考文献
    相似文献
    引证文献
引用本文

Shi Xiaohong, Zeng Xierong, Li Hejun, Fu Qiangang, Zou Jizhao. TaSi2 Oxidation Protective Coating for SiC Coated Carbon/Carbon Composites[J].稀有金属材料与工程,2011,40(3):403~406.[Shi Xiaohong, Zeng Xierong, Li Hejun, Fu Qiangang, Zou Jizhao. TaSi2 Oxidation Protective Coating for SiC Coated Carbon/Carbon Composites[J]. Rare Metal Materials and Engineering,2011,40(3):403~406.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2010-03-25
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: