Influences of Secondary Phase Mg3Hg Compound on the Electrochemical Properties of the Mg-5%Hg-1%Ga Alloys
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用熔炼铸造方法制备出Mg-5%Hg-1%Ga合金,在573~773 K时效不同时间,利用X射线物相检测、扫描电镜结合能谱分析第二相Mg3Hg的形貌和分布,用交流阻抗法等电化学方法研究Mg3Hg对Mg-5%Hg-1%Ga阳极在3.5%NaCl(质量分数)溶液中电化学性能的影响。结果表明:时效时间从15 min延长至200 h时,Mg-5%Hg-1%Ga合金中α-Mg和Mg3Hg的共晶组织转变为α-Mg基体中弥散分布Mg3Hg颗粒,这种转变降低了浓差极化和法拉第反应中电荷传递电阻,提高电化学活性。弥散分布的Mg3Hg颗粒使Mg-5%Hg-1%Ga合金组织均匀,提高了耐腐蚀性能。

    Abstract:

    The Mg-5%Hg-1%Ga alloy was prepared by melting-casting. Aging at 573-773 K for different time were carried out to ensure the fine dispersion of Mg3Hg compounds. Scanning electron microscopy (SEM), emission spectrometry (ESA) and X-ray diffraction (XRD) were employed to characterize the morphology and distribution of the secondary phase Ma3Hg. The electrochemical and corrosion behaviors of the alloy in 3.5wt% NaCl solution was studied by means of potentiodynamic, galvanostatic and electrochemical impedance spectroscopy (EIS) measurements. The relationship between the Mg3Hg compound and the electrochemical properties of the Mg-5%Hg-1%Ga alloy was discussed. The results demonstrate that when the aging time increases from 15 min to 200 h, the intergranular eutectic of α-Mg and Mg3Hg changes into dispersed Mg3Hg particles in α-Mg matrix. This transition increases electrochemical activity of Mg-5%Hg-1%Ga alloy due to the decreased concentration polarization and charge transfer resistance in the faradaic reaction. The electrochemical homogeneity of the microstructure increases the corrosion resistance of the Mg-5%Hg-1%Ga alloy.

    参考文献
    相似文献
    引证文献
引用本文

冯 艳,王日初,彭超群,王乃光.第二相Mg3Hg对Mg-5%Hg-1%Ga合金电化学性能的影响[J].稀有金属材料与工程,2011,40(6):1010~1014.[Feng Yan, Wang Richu, Peng Chaoqun, Wang Naiguang. Influences of Secondary Phase Mg3Hg Compound on the Electrochemical Properties of the Mg-5%Hg-1%Ga Alloys[J]. Rare Metal Materials and Engineering,2011,40(6):1010~1014.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2010-09-15
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: