Effects of Withdrawal Rate on Solidification Microstructure of Single Crystal Ni-based Superalloy Containing Ruthenium
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    研究了不同抽拉速率对含Ru镍基单晶高温合金凝固组织的影响。结果表明,随着抽拉速率的加快,单晶合金的铸态组织由粗枝状晶向细枝状晶演变,枝晶干和枝晶间的g ¢相尺寸减少,合金元素的偏析降低,g-g ¢共晶含量减少,NiAl基b相含量逐渐降低。同时,抽拉速率对合金的相变温度影响不大。

    Abstract:

    The effect of withdrawal rates on the solidification microstructure of a single crystal Ni-based superalloy containing ruthenium was investigated. The results show that with the increase of the withdrawal rate, the as-cast microstructure of the single crystal alloy transforms from coarse dendrite to fine dendrite. Meanwhile, the size of the g ¢ particles decreases, segregation of alloying elements for the dendrite and interdendritic regions tends to be reduced, the volume fraction of g-g ¢ eutectic and NiAl-based b phase decreases gradually. In addition, the withdrawal rate has little influence on the phase transformation temperature of the superalloy.

    参考文献
    相似文献
    引证文献
引用本文

刘丽荣,茆 亮,陈立佳,金 涛,胡壮麒.抽拉速率对含Ru镍基单晶高温合金凝固组织的影响[J].稀有金属材料与工程,2011,40(12):2212~2215.[Liu Lirong, Mao Liang, Chen Lijia, Jin Tao, Hu Zhuangqi. Effects of Withdrawal Rate on Solidification Microstructure of Single Crystal Ni-based Superalloy Containing Ruthenium[J]. Rare Metal Materials and Engineering,2011,40(12):2212~2215.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2010-12-25
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期: