Mg-8.5Li-3Al-xCe系合金的时效行为研究
基金项目:

黑龙江省自然科学基金 (E200913); 黑龙江省教育厅科研项目 (11551477); 佳木斯大学人才培养项目 (RC2009-035)

  • 摘要
  • | |
  • 访问统计
  • | |
  • 相似文献
  • | | |
  • 文章评论
    摘要:

    采用真空感应熔炼技术制备Mg-8.5Li-3Al-xCe(x=0, 1, 3)合金。研究Mg-8.5Li-3Al-xCe系合金的时效行为。结果表明,Ce对时效硬化程度具有显著的影响,随Ce含量的增加合金在各时期的硬度都增大,最高时效峰硬度也随之提高,过时效软化的程度随之降低。Ce抑制时效硬化相MgLi2Al和时效软化相AlLi相的生成是Mg-8.5Li-3Al-xCe系合金时效硬化及过时效软化程度降低的主要原因,Ce是抑制Mg-Li-Al合金发生时效软化的有益元素

    Abstract:

    Mg-8.5Li-3Al-xCe (x=0, 1, 3) alloys were prepared with vacuum induction melting method. Then the aging behavior of the Mg-8.5Li-3Al-xCe alloy was investigated. The results show that Ce has an obvious effect on the aging-hardening process. With the increase of Ce content, the aging hardness increases and the over-aging softening is suppressed to some extent. The aging hardness increase and the over-aging softening decrease of Mg-8.5Li-3Al-xCe (x=0, 1, 3) alloys is mainly attributed to that Ce inhibits the generation of age-hardening phase MgLi2A1 and over-aging softening phase AlLi. Ce can hinder the over-aging process in Mg-Li-Al alloys

    参考文献
    相似文献
    引证文献
    网友评论
    网友评论
    分享到微博
    发 布
引用本文

王 涛,张密林,巫瑞智,赵淑金. Mg-8.5Li-3Al-xCe系合金的时效行为研究[J].稀有金属材料与工程,2013,42(1):94~98.[Wang Tao, Zhang Milin, Wu Ruizhi, Zhao Shujin. Aging Behavior of Mg-8.5Li-3Al-xCe Alloy[J]. Rare Metal Materials and Engineering,2013,42(1):94~98.]
DOI:[doi]

复制
文章指标
  • 点击次数:1364
  • 下载次数: 0
  • HTML阅读次数: 138
  • 引用次数: 0
历史
  • 收稿日期:2012-01-16