超细晶纯钛阳极氧化表面性能研究

Study on Properties of Anodic Oxidized Surface of Ultrafine-Grained Titanium

摘要:

研究了常规纯钛和超细晶纯钛阳极氧化表面的形貌、膜-基结合力、抗腐蚀性能和微动摩擦磨损性能。结果表明：与常规纯钛氧化表面相比，超细晶纯钛氧化表面具有更多纳米尺度孔穴，更高的膜-基结合力（后者是前者的2倍），更高的抗模拟体液电化学腐蚀性能（后者的腐蚀速率是前者的2/5），更低的摩擦系数（0.12:0.34）、更高的耐磨性。分析认为，以上性能变化是纯钛组织超细化提高其晶体缺陷（内能）所致

Abstract:

The surface morphology, the film-substrate bonding force, the corrosion resistance and the fretting friction and wear properties of anodic oxidized surface of conventional Ti and ultrafine-grained Ti were investigated. The results show that compared to the anodic oxidized surface of conventional Ti, the anodic oxidized surface of ultrafine-grained titanium exhibits a more nano-scale cavities, a higher film-substrate bonding force (bonding force of the latter is 2 times of the former), a higher corrosion resistance (corrosion rate of the latter is 2/5 of the former), a lower friction coefficient (0.12 vs 0.34) and a higher wear resistance. It is believed that these above mentioned improvements are caused by the increasement of crystal defects (internal energy) due to microstructure ultrafinement.