淬火-回火工艺对Ti-46Al-xB合金柱状晶组织的影响
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

基金项目:

黑龙江省自然科学基金项目(201131); 黑龙江省教育厅科学技术研究项目(12521445); 黑龙江工程学院博士科研基金项目(2011BJ12)


Effect of Quenching-Tempering Technology on Columnar Structure in Ti-46Al-xB Alloys
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    研究了淬火-回火工艺对Ti-46Al-xB合金柱状晶组织的影响。研究发现,淬火-回火工艺对Ti-46Al-xB合金的柱状晶组织具有明显的细化效果。这主要是由于温度梯度的增加和冷却过程中发生固态相变使晶界或相界面上原子错配,从而形成大量的位错,位错对晶界具有“钉扎”作用,从而细化TiAl基合金柱状晶组织。结果表明,通过合金化元素B和热处理工艺的共同作用可以获得更为细小的TiAl基合金柱状晶组织。这主要是由于随着B含量的增加,硼化物的析出量增加,而硼化物对位错线的进一步扩展起到了阻碍作用。从而促进了位错对晶界的“钉扎”作用,进一步细化了TiAl基合金柱状晶组织

    Abstract:

    The effect of the quenching-tempering process on the columnar structure in Ti-46Al-xB alloys was investigated. It is found that the columnar structures of Ti-46Al-xB alloys are evidently refined by the quenching-tempering process. The reason is that the increase of the temperature gradient and the solid state phase transformation during cooling process lead to atomic mismatch in grain boundary or phase interface, and then a large number of dislocations are formed, which can pin the grain boundary. The experimental results show that finer columnar structure of TiAl-based alloys can be obtained by addition of alloying element B and the heat treatment process. Besides, the addition of B element can impede the extension of dislocations, promoting the effect of anchoring of dislocation, and then the columnar structures are further refined in TiAl-based alloys

    参考文献
    相似文献
    引证文献
引用本文

杨慧敏,骆良顺,宋美慧,齐海群,王春艳,杨 闯,苏彦庆.淬火-回火工艺对Ti-46Al-xB合金柱状晶组织的影响[J].稀有金属材料与工程,2014,43(11):2774~2777.[Yang Huimin, Luo Liangshun, Song Meihui, Qi Haiqun, Wang Chunyan, Yang Chuang, Su Yanqing. Effect of Quenching-Tempering Technology on Columnar Structure in Ti-46Al-xB Alloys[J]. Rare Metal Materials and Engineering,2014,43(11):2774~2777.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2013-11-20
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2015-04-07
  • 出版日期: