Influence of Temperature and Loading Rates on Deformation Behaviors
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    研究了淬火和时效2种状态的U-5.7%Nb合金,从室温(20 ℃)~800 ℃温度范围的准静态拉伸性能,及合金的变形和断裂行为。结果表明,不论淬火或时效状态的U-5.7%Nb合金,当温度高于200 ℃后,合金在室温下表现出的二次屈服现象将完全消失,并在400 ℃温度附近发生脆化,在700 ℃温度附近表现出明显的超塑性,其中淬火态合金性能的变化尤为明显。并对准静态拉伸、Hopkinson拉伸及爆炸膨胀环3种加载速率下,时效态U-5.7%Nb合金的组织结构进行了对比分析。结果表明,以不同应变速率断裂的时效态U-5.7%Nb合金,断口中心部位的韧窝比边缘部位相对明显,Hopkinson拉伸断口的晶粒大于准静态拉伸断口的晶粒,爆炸速率断裂的合金断口有剪切断裂、边缘开裂及局部夹杂脱落的现象

    Abstract:

    Quasi-static tensile properties, deformation and fracture behaviors of both quenched and aged U-5.7%Nb alloys in a temperature range from room temperature to 800 oC were investigated. The results show that the second yield phenomenon of both quenched and aged U-5.7%Nb alloys occurring at room temperature disappeared at a temperature higher than 200 oC, and the embrittlement behaviors of two alloys appeared at 400 oC. Meanwhile, the superplasticity has been observed in two alloys at the temperature higher than 700 oC, and the superplasticity of the quenched alloys was more evident than that of the aged alloys. The microstructures of the aged U-5.7%Nb deformed at quasi-static tension, Hopkinson tension and expansion loadings have been analyzed. The results indicate that the dimples at the center zone of the specimens were more obvious than that at the rim zone in aged U-5.7%Nb alloys fractured at different strain rates. And the grains at the fracture of Hopkinson tension were larger than that of the quasi-static loading. Shear fracture, rim cracking and inclusion falling off were observed in the fracture of the alloys deformed at expansion loading

    参考文献
    相似文献
    引证文献
引用本文

邱志聪,何立峰,肖大武,邹东利,杨江荣.温度及加载速率对U-5.7%Nb合金变形行为的影响[J].稀有金属材料与工程,2014,43(11):2829~2835.[Qiu Zhicong, He Lifeng, Xiao Dawu, Zou Dongli, Yang Jiangrong. Influence of Temperature and Loading Rates on Deformation Behaviors[J]. Rare Metal Materials and Engineering,2014,43(11):2829~2835.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2013-11-15
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2015-04-07
  • 出版日期: