原位β-Zr相/Zr非晶基复合材料的干摩擦滑动磨损行为
DOI:
作者:
作者单位:

辽宁工业大学材料科学与工程学院,辽宁工业大学材料科学与工程学院,辽宁工业大学材料科学与工程学院

作者简介:

通讯作者:

中图分类号:

基金项目:

辽宁省教育厅资助项目(L2013250)


Dry Sliding Wear Behavior of in-Situ β-Zr/ Zr-Based Metallic Glass Matrix Composites underSDrySSlidingSCondition
Author:
Affiliation:

School of Materials Science and Engineering,Liaoning University of Technology,School of Materials Science and Engineering,Liaoning University of Technology,School of Materials Science and Engineering,Liaoning University of Technology

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用铜模喷铸法制备出直径为3mm的原位β-Zr相/Zr非晶基复合材料,对其在干摩擦条件下的滑动磨损行为进行了研究。结果表明,与纯块状非晶合金相比, Zr基块状非晶复合材料的耐磨性能得到明显的改善。复合材料比纯块状非晶合金具有更低的摩擦系数和磨损速度,最低的磨损速度比纯非晶合金的减小48.1%。同时,包含一定体积分数β-Zr相的复合材料表面磨损比纯非晶合金的轻,只有一些浅的犁沟,其磨削小,显示出轻微的磨粒磨损特征,而纯非晶合金的磨损表面呈现出片状、分层、凸起及深的犁沟等特征,磨削大,为严重的磨粒磨损。复合材料低的磨损速度归因于铸态下析出的分布在非晶基体上的韧性β-Zr枝晶相的存在。该相具有较强的承载、塑性变形和加工硬化能力,通过减小界面处非晶基体的应力集中、释放应变能、限制剪切带和裂纹的萌生与扩展、使塑性变形更加均匀等途径提高耐磨性能。

    Abstract:

    In-situ β-Zr/ Zr-based metallic glass matrix composites with diameter of 3 mm were fabricated by conventional Cu-mold casting method and the wear behavior underSdrySslidingScondition of the composites were investigated. The results indicate that compared to the pure BMG, the composites exhibited a markedly improved wear resistance. The composites showed lower friction coefficient and wear rate than the pure BMG. The lowest wear rate in these composites is 48.1% lower than that of the pure BMG. Meanwhile, the worn surface of a proper amount of composite is less severe and there were shallow grooves with some fine wear debris on the worn surface, which exhibited the characteristic of mild abrasive, whereas that of the pure BMG is characterized by flakes, delamination, pile-up and deep grooves which show a severe abrasive wear mode. The improvement of the wear resistance of the composites is attributed to the fact that the β-Zr crystalline phase distributed in the amorphous matrix has some effective load bearing, plastic deformation and work hardening ability to decrease strain accumulation and the release of strain energy in the glassy matrix, restrict the expanding of shear bands and cracks, and occur plastic deformation homogeneously.

    参考文献
    相似文献
    引证文献
引用本文

武晓峰,张广安,伍复发.原位β-Zr相/Zr非晶基复合材料的干摩擦滑动磨损行为[J].稀有金属材料与工程,2017,46(4):1086~1091.[Wu Xiaofeng, Zhang Guangan, Wu Fufa. Dry Sliding Wear Behavior of in-Situ β-Zr/ Zr-Based Metallic Glass Matrix Composites underSDrySSlidingSCondition[J]. Rare Metal Materials and Engineering,2017,46(4):1086~1091.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2015-01-11
  • 最后修改日期:2015-05-29
  • 录用日期:2015-08-11
  • 在线发布日期: 2017-08-04
  • 出版日期: