Ni掺杂SnO2的光谱特性及气敏性能研究
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

基金项目:

辽宁省教育厅科研计划项目(L2013203);中央高校基本科研业务费项目 (3132013085)


Spectroscopic Analysis and Gas Sensing Performance of Ni-doped SnO2
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用溶剂热法将Ni掺杂到纳米SnO2中,分别利用TEM、EDAX、XRD、Raman和XPS表征了Ni掺杂后SnO2的微观形貌、结构和元素组成特征,分析了Ni掺杂对增强SnO2气敏性能的作用机理。实验结果表明,Ni的掺杂可抑制SnO2晶粒增长,减小SnO2晶粒尺寸,进而提升传感器的气敏性能。少量的Ni掺杂能够使Ni2+进入SnO2晶格中取代Sn4+产生氧空位,促进SnO2气敏性能的提高;而当Ni掺杂量达到30%时,会导致部分Ni以其他的形式存在于SnO2晶体表面上,降低SnO2气敏性能

    Abstract:

    Ni-doped SnO2 powders were prepared by the solvethermal method. The morphology, structure and elemental composition of Ni-doped SnO2 were characterized by TEM, EDAX, XRD, Raman and XPS. Gas sensing properties of Ni-doped SnO2 were also investigated by sensitivity measurements. The results show that Ni doping inhibits the grain growth of SnO2 and decreases the grain size, thus enhancing the gas sensitivity of SnO2. Oxygen vacancies formed by the substitution of Ni2+ for Sn4+ in the SnO2 matrix improves the gas sensing performance at low level of Ni doping. However, when Ni concentration reaches 30 wt%, the addition of Ni to SnO2 decreases gas sensitivity, which is attributed to the counteraction of the n- and p-type sensors

    参考文献
    相似文献
    引证文献
引用本文

肖井坤,宋成文,张肖妮,初 璇,吴帅华,成慕荣,宋明艳,于迎涛. Ni掺杂SnO2的光谱特性及气敏性能研究[J].稀有金属材料与工程,2015,44(10):2509~2512.[Xiao Jingkun, Song Chengwen, Zhang Xiaoni, Chu Xuan, Wu Shuaihua, Cheng Murong, Song Mingyan, Yu Yingtao. Spectroscopic Analysis and Gas Sensing Performance of Ni-doped SnO2[J]. Rare Metal Materials and Engineering,2015,44(10):2509~2512.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2014-10-28
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2016-07-13
  • 出版日期: