Research on Measurement of Residual Stress of Welded 5A06 Aluminum Alloy Based on Synchrotron Radiation Diffraction Technology
Author:
Affiliation:

1.University of Science Technology Beijing;2.Beijing Satellite Manufactory Company Limited

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文利用同步辐射X射线衍射技术测量了变极性等离子弧(VPPA)焊接5A06铝合金试样表面的残余应力,获得了该试样表面残余应力的分布规律,结合金相组织观察、EBSD、显微硬度测试等方法,分析了焊缝区、热影响区、母材区残余应力的产生及演化机制。结果表明:VPPA焊接5A06板材焊缝区晶粒粗大,热影响区晶粒细小,残余应力呈现出焊缝区域为压应力,热影响区为拉应力的“M”形状;在垂直于焊缝(TD)方向上存在75.79MPa的最大拉应力和159.34MPa的最大压应力;在平行于焊缝(LD)方向上存在为132.33MPa的最大拉应力和89.38MPa的最大压应力。相比于传统X射线仪器测量获得的残余应力变化趋势,同步辐射衍射测量的残余应力分布趋势与试样不同焊接区域显微硬度的变化趋势更加吻合。实验结果表明,相比于传统的X射线仪器测量残余应力,同步辐射X射线衍射测量的残余应力数据一致性更好。

    Abstract:

    The residual stress on surface of variable polarity plasma arc (VPPA) weldedS5A06 aluminium alloy sampleSwas measured by synchrotron radiation X-ray diffraction, and the distribution of residual stress on the surface of the sample was obtained in this paper. The generation and evolution mechanisms of weld zone, heat affected zone, base metal area were analyzed in combination with metallurgical structureSobservation, EBSD and microhardness tester methods. The results show that the weld zone of VPPA welded 5A06 plate shows coarse grainS, the grains in the heat affected zone are small, the residual stress presents an "M" shape: the weld zone is compressive stress, and the heat affected zone is tensile stress; There is a maximum tensile stress of 75.79 MPa and a maximum compressive stress of 159.34 MPa in the direction vertical weld (TD) and a maximum tensile stress of 132.33 MPa and a maximum compressive stress of 89.38 MPa in the direction parallel to the weld (LD). Compared with the trend of the residual stress measured by traditional X-ray instrument, the distribution trend of the residual stress of the synchrotron radiation diffraction measurement is more consistent with the variation trend of the microhardness of the sample in different welding areas. The experimental results show that the residual stress data of synchrotron radiation X-ray diffraction measurement has better consistency than the traditional X-ray instrument.

    参考文献
    相似文献
    引证文献
引用本文

杨斌,韩月林,蔡泉,杨光辉,祁俊峰.基于同步辐射衍射技术的5A06铝合金焊接残余应力的测量研究[J].稀有金属材料与工程,2019,48(1):205~212.[Yang Bin, Han Yuelin, Cai Quan, Yang Guang hui, Qi Jun feng. Research on Measurement of Residual Stress of Welded 5A06 Aluminum Alloy Based on Synchrotron Radiation Diffraction Technology[J]. Rare Metal Materials and Engineering,2019,48(1):205~212.]
DOI:10.12442/j. issn.1002-185X.20180387

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-04-17
  • 最后修改日期:2018-07-11
  • 录用日期:2018-07-12
  • 在线发布日期: 2019-02-18
  • 出版日期: