Ni-Cr-W三元系富Ni侧fcc相的互扩散及原子迁移率参数研究
作者:
作者单位:

厦门大学材料学院及福建省材料基因工程重点实验室

作者简介:

通讯作者:

中图分类号:

TG14

基金项目:

国家重点研发计划(2016YFB0701401),国家自然科学基因面上项目(51771158),(51471138)。


Interdiffusion and Atomic Mobilities in Ni-rich fcc Ni-Cr-W Alloys
Author:
Affiliation:

Fund Project:

National Key R&D Program of China (2016YFB0701401), National Natural Science Foundation of China (51771158 and 51471138)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    利用电子探针微量分析与Whittle and Green方法确定了在1200℃下退火72小时的三元合金Ni-Cr-W体系的互扩散系数。通过DICTRA软件包对实验互扩散系数进行评估以确定原子迁移率。通过全面分析比较模型预测的扩散特性和实验数据,良好一致性验证了原子迁移率参数的合理性。 Ni-Cr-W三元体系中的扩散现象,如扩散路径和浓度-距离曲线可以通过目前获得的原子迁移率合理地描述,进一步证明了本研究所获得的原子迁移率参数的可靠性。

    Abstract:

    Six diffusion couples of Ni-Cr-W ternary alloys were prepared, annealed at 1473 K for 72 hours and measured by using the electron probe microanalysis combined with Whittle and Green method in order to determine the interdiffusion coefficients. The experimental interdiffusion coefficients were critically assessed to obtain the atomic mobilities by means of DICTRA software package. A good agreement has been obtained by comprehensive comparison between the experimental data and the model-predicted diffusion properties, which verifies the reliability of the atomic mobilities of Ni, Cr and W in Ni-Cr-W alloys. The diffusion phenomena, such as diffusion paths and the concentration-distance profiles in the Ni-Cr-W ternary system can be reasonably described by the presently obtained atomic mobilities.

    参考文献
    相似文献
    引证文献
引用本文

王翠萍,秦诗洋,卢勇,魏振帮,于金鑫,邹宏伟,杨水源,韩佳甲,刘兴军. Ni-Cr-W三元系富Ni侧fcc相的互扩散及原子迁移率参数研究[J].稀有金属材料与工程,2020,49(2):441~446.[wangcuiping, Qin Shiyang, Lu Yong, Wei Zhenbang, Yu Jinxin, Zou Hongwei, Yang Shuiyuan, Han Jiajia, Liu Xingjun. Interdiffusion and Atomic Mobilities in Ni-rich fcc Ni-Cr-W Alloys[J]. Rare Metal Materials and Engineering,2020,49(2):441~446.]
DOI:10.12442/j. issn.1002-185X.20180964

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-09-17
  • 最后修改日期:2018-11-08
  • 录用日期:2018-11-09
  • 在线发布日期: 2020-03-12
  • 出版日期: