涂覆载量对IrO2-CeO2-G/Ti电极组织结构和电容性能的影响

Effect of IrO2 Content on Microstructure and Capacitance of IrO2-CeO2-G/Ti Electrode

摘要:

采用热分解法制备了新型IrO2-CeO2-G/Ti复合电极。采用SEM、TEM、XRD和XPS等测试手段分别对不同IrO2含量的电极进行表征。采用循环伏安法、恒流充放电法和电化学阻抗谱法对电极的电化学行为进行研究。结果表明，IrO2涂覆载量为2.5mg/cm2 的电极具有最大的比电容值459.5 F/g。在5mA/cm2电流密度下，经5000次充放电循环后IrO2涂覆载量为2.5mg/cm2电极比电容仍能保持97.8%。该种复合电极材料因其独特的元素组成和良好的赝电容性能，是一种理想的超级电容器电极材料。

Abstract:

The novel IrO2-CeO2-G/Ti composite electrodes were prepared by thermal decomposition method. The synthesized electrodes with different IrO2 content had been characterized by scanning electron microscope(SEM), transmission electron microscope(TEM), X-ray diffraction(XRD) and X-ray photoelectron spectroscopy(XPS). The electrochemical performances of the electrodes were investigated by cyclic voltammetry, galvanostatic charge–discharge and electrochemical impedance spectroscopy in 0.5 M H2SO4 solution. The results showed that the electrode with 2.5mg/cm2 IrO2 exhibited an excellent specific capacitance value of 459.5 F/g, and the specific capacitance maintained about 97.8% after 5000 charge-discharge cycles at a 5mA/cm2 current density. The electrode with 2.5mg/cm2 IrO2 was an ideal electrode for supercapacitor due to?its unique composition proportion and the excellent pseudocapacitance property.