基板材料对激光熔化沉积制造Ti-48Al-2Cr-2Nb合金组织、织构、相和显微硬度的影响
作者:
作者单位:

沈阳工业大学材料科学与工程学院

作者简介:

通讯作者:

中图分类号:

基金项目:

智能化增材制造系统平台 (2017YFB1103600)


Effect of substrate material on the microstructure, texture, phase and microhardness of a Ti-48Al-2Cr-2Nb alloy processed by laser melting deposition
Author:
Affiliation:

School of Materials, Shenyang University of Technology

Fund Project:

Intelligent Additive Manufacturing System Platform (2017YFB1103600)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文研究了基体材料对激光熔化沉积Ti-48Al-2Cr-2Nb合金显微组织、织构、相组成和硬度的影响。随着沉积层数的增加,沉积层的显微组织由网篮状结构向等轴状结构转变,最终演变为层状结构。α2(Ti3Al)相逐渐减少,γ(TiAl)相逐渐增多。不同的TiAl合金层具有不同的显微硬度。随着沉积层数的增加,显微硬度降低。研究结果对于激光沉积制造TiAl合金制备具有可接受的组织、织构、相组成和显微硬度具有参考价值。

    Abstract:

    Effect of substrate material on the microstructure, texture, phase and hardness of a Ti-48Al-2Cr-2Nb alloy processed by laser melting deposition (LMD) was investigated. With the increase of the number of deposited layers, the microstructure of the deposited layers changes from basket structure to equiaxed structure and finally evolves into lamellar structure, and α2 (Ti3Al) phase decreases and γ (TiAl) phase increases gradually. Different TiAl alloy layers show different microhardness. With the increase of the number of deposited layers, the microhardness decreases. The findings would be a valuable reference for fabricating TiAl components with acceptable microstructure, texture, phase compositions and microhardness by LMD.

    参考文献
    相似文献
    引证文献
引用本文

刘占起,马瑞鑫,王文博,徐国建,苏允海.基板材料对激光熔化沉积制造Ti-48Al-2Cr-2Nb合金组织、织构、相和显微硬度的影响[J].稀有金属材料与工程,2020,49(7):2262~2268.[Liu Zhanqi, Ma Ruixin, Wang Wenbo, Xu Guojian, Su Yunhai. Effect of substrate material on the microstructure, texture, phase and microhardness of a Ti-48Al-2Cr-2Nb alloy processed by laser melting deposition[J]. Rare Metal Materials and Engineering,2020,49(7):2262~2268.]
DOI:10.12442/j. issn.1002-185X.20190278

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-04-01
  • 最后修改日期:2019-05-14
  • 录用日期:2019-06-14
  • 在线发布日期: 2020-08-31
  • 出版日期: