Tribological properties of CrN/TiN superlattice coatings deposited by deep oscillation magnetron sputtering
Author:
Affiliation:

Tsinghua University

Fund Project:

National Natural Science Foundation Joint Fund Key Project(U1865206),National Science and Technology Major Project(2017- VII-0012-0107),National Defense Science and Technology Key Laboratory Fund (614220207011802),Guangdong Province Key Area R&D Program (2019B090909002)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文研究了IN 718高温合金、WC-6%Co硬质合金和Si(100) 基体上深振荡磁控溅射复合沉积CrN/TiN超晶格涂层的摩擦学性能。研究表明,涂层的生长对基体的类型没有选择性。随着基体的硬度升高,划痕结合力失效临界载荷增大,涂层结合力失效机制由翘曲失效转变为基体/涂层协同变形,未发现涂层的剥落失效。载荷为2 N时,磨损机制由磨粒磨损和氧化磨损转变为轻微磨粒磨损。载荷为4 N时,IN718基体上涂层的磨损机制为严重的氧化磨损,WC-6%Co基体上的涂层的磨损机制为磨粒磨损和氧化磨损,氧化物的产生、堆积和转移导致摩擦系数的波动。

    Abstract:

    ). In this work, tribological properties of CrN/TiN superlattice coatings deposited on IN 718, WC-6%Co and Si(100) by the combined deep oscillation magnetron sputtering was investigated. Results show that the coating growth was independent of the nature of substrate materials. As the hardness of substrate materials was increased, the scratch critical loads increased. Adhesion failure mode changed from buckling failure to cooperative deformation of substrate/coating system with only small cracks in the whole scratch track. Wear mechanism of the coatings deposited on IN 718 and WC-6%Co changed from abrasive wear and oxidative to mild abrasive wear at a normal load of 2 N. Under normal load of 4 N, the coatings on IN 718 suffered serve oxidative wear, while the coatings on WC-6%Co suffered the combined abrasive and oxidative wear. The production, accumulation and mass transfer of oxides resulted in the oscillation of friction coefficient during dry sliding wear tests.

    参考文献
    相似文献
    引证文献
引用本文

欧伊翔,庞盼,罗军,廖斌,雷明凯,欧阳晓平.深振荡磁控溅射复合沉积CrN/TiN超晶格涂层的摩擦学性能[J].稀有金属材料与工程,2020,49(7):2476~2479.[Ou Yixiang, Pang Pan, Luo Jun, Liao Bin, Lei Mingkai, Ouyang Xiaoping. Tribological properties of CrN/TiN superlattice coatings deposited by deep oscillation magnetron sputtering[J]. Rare Metal Materials and Engineering,2020,49(7):2476~2479.]
DOI:10.12442/j. issn.1002-185X.20190525

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-06-20
  • 最后修改日期:2019-09-16
  • 录用日期:2019-10-11
  • 在线发布日期: 2020-08-31
  • 出版日期: