烧结温度对(Ti, W, Mo, Nb)(C, N)-(Co, Ni)金属陶瓷组织结构和性能的影响
作者:
作者单位:

1.福州大学材料科学与工程学院;2.鲁汶大学材料工程系;3.福建工程学院材料科学与工程学院

作者简介:

通讯作者:

中图分类号:

基金项目:

University-Industry cooperation project of Fujian Province(2019H6022)


Effect of sintering temperature on the microstructure and machining performance of (Ti, W, Mo, Nb)(C, N)-(Co, Ni) cermets
Author:
Affiliation:

College of Materials Science and Engineering, Fuzhou University

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文以(Ti,W,Mo,Nb)(C,N)-(Co,Ni)基金属陶瓷材料为研究对象,研究烧结温度对金属陶瓷的成分、微观组织和力学性能的影响,初步探讨成分、微观组织与材料强度的关系。研究结果表明:烧结温度对(Ti,W,Mo,Nb)(C,N)-(Co,Ni)基金属陶瓷组织特征有显著的影响;合金的总碳(Ct%)随着烧结温度的提高而降低,当烧结温度达到1490℃时,合金总碳的急剧降低,导致合金组织中出现脱碳相(η相),从而使得合金的硬度(HV30) 、断裂韧性(KIC)和抗弯强度(TRS)降低;1470℃烧结温度下,(Ti,W,Mo,Nb)(C,N)-(Co,Ni)基金属陶瓷合金的硬度(HV30) 、断裂韧性(KIC)和抗弯强度(TRS)的匹配最佳,表现为在实际应用工况下的综合切削性能最优。

    Abstract:

    In this study, dense Co- and Ni-bonded Ti(C0.6N0.4) matrix cermets with secondary carbides, i.e., WC, Mo2C, and NbC, were prepared using liquid phase sintering in vacuum for 60 min at temperatures ranging from 1410 to 1490°C. The detailed microstructural and phase analysis was performed using scanning electron microscopy, electron probe microanalysis, and X-ray diffraction analysis. The effect of sintering temperature on the microstructure, mechanical properties, and machining performance of cermets was investigated. The results showed that sintering temperature had a significant impact on the microstructural characteristics of (Ti, W, Mo, Nb)(C, N)-(Co, Ni) cermets. The total carbon content of cermets decreased with increase in temperature and a carbon-deficient phase (M6C) was observed in the cermet sintered at 1490°C. The cermets sintered at temperatures of up to 1470°C were composed of an fcc solid solution metal binder and two types of core-rim structured grains, i.e., cubic carbide solution and cubic Ti(C, N) solution phases. The best machining performance on continuous / interrupted turning was found in the cermet sintered at 1470°C because of an optimum combination of hardness and transverse rupture strength.

    参考文献
    相似文献
    引证文献
引用本文

项忠楠,李战江,黄水根,常发,戴品强.烧结温度对(Ti, W, Mo, Nb)(C, N)-(Co, Ni)金属陶瓷组织结构和性能的影响[J].稀有金属材料与工程,2021,50(4):1179~1186.[xiang zhong nan, Li Zhan jiang, Huang Shui gen, Chang Fa, Dai Pin qiang. Effect of sintering temperature on the microstructure and machining performance of (Ti, W, Mo, Nb)(C, N)-(Co, Ni) cermets[J]. Rare Metal Materials and Engineering,2021,50(4):1179~1186.]
DOI:10.12442/j. issn.1002-185X.20200228

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2020-04-06
  • 最后修改日期:2020-04-27
  • 录用日期:2020-05-08
  • 在线发布日期: 2021-05-08
  • 出版日期: