Study on the Microstructures and Properties of AlxTiCrMnCu High Entropy Alloys Fabricated by Laser Deposition
Author:
Affiliation:

1.School of Materials Science and Engineering,East China Jiaotong University

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用激光沉积方法制备了AlxTiCrMnCu (x=0, 0.25, 0.5, 0.75, 1.0)高熵合金。通过XRD、SEM及腐蚀电化学测试技术等研究了AlxTiCrMnCu高熵合金的微观结构及性能。研究发现,随Al含量的增加,AlxTiCrMnCu高熵合金由简单的FCC和HCP1混合固溶体结构逐渐转变为全部HCP2固溶体结构;合金的显微硬度随Al含量的增加而增大;AlxTiCrMnCu高熵合金在3.5% NaCl水溶液中的耐蚀性先提高后降低,当x=0.25时,其耐蚀性最佳。

    Abstract:

    AlxTiCrMnCu (x=0, 0.25, 0.5, 0.75, 1.0) high entropy alloys were prepared by laser deposition. The XRD、SEM and corrosion electrochemical testing methods were used to investigate the effect of Al on the microstructure and properties of AlxTiCrMnCu alloys. The results show that, with the increase of Al addition, phases of AlxTiCrMnCu alloys change from simple FCC and HCP1 solid-solutions to single HCP2 solid-solution. The microhardness of AlxTiCrMnCu alloys increases gradually with the increase of Al addition. The corrosion resistance of AlxTiCrMnCu alloys in 3.5% NaCl solution increases firstly and then decreases with the increase of Al addition. The optimum corrosion resistance can be obtained when x=0.25.

    参考文献
    相似文献
    引证文献
引用本文

胡勇,刘飞,王达豪,赵龙志,唐延川,刘德佳,沈明学,赵火平,焦海涛.激光沉积AlxTiCrMnCu高熵合金组织性能的研究[J].稀有金属材料与工程,2021,50(8):2967~2972.[Hu Yong, Liu Fei, Wang Dahao, Zhao Longzhi, Tang Yanchuan, Liu Dejia, Shen Mingxue, Zhao Huoping, Jiao Haitao. Study on the Microstructures and Properties of AlxTiCrMnCu High Entropy Alloys Fabricated by Laser Deposition[J]. Rare Metal Materials and Engineering,2021,50(8):2967~2972.]
DOI:10.12442/j. issn.1002-185X.20200693

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2020-09-11
  • 最后修改日期:2020-10-10
  • 录用日期:2020-10-23
  • 在线发布日期: 2021-09-07
  • 出版日期: 2021-08-31