轧制工艺对TC4合金板材织构演变及组织性能的影响
作者:
作者单位:

北京科技大学工程技术研究院

作者简介:

通讯作者:

中图分类号:

基金项目:

国家重点研发计划重点专项(2016YFB0301200)


Effect of rolling process on texture evolution, microstructure and mechanical properties of TC4 alloy plate
Author:
Affiliation:

Institute of Engineering Technology,University of Science and Technology Beijing

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文研究了顺向冷轧和换向冷轧两种轧制方式对TC4板材显微组织、织构和力学性能的影响规律。研究结果表明:两种轧制工艺的晶粒都有所细化;顺向冷轧微观组织仍存在带状组织,α晶粒呈现出方向性的拉长;换向冷轧晶粒破碎的更加均匀,退火后形成的细小等轴α晶粒。换向冷轧工艺的塑性指标显著优于顺向冷轧,强度指标略低于顺向冷轧,但是板材的RD和TD之间的差值明显减少。原始冷轧板材主要存在(-12-10)<10-10>棱锥型织构,强度较高;顺向冷轧遗传了原始板材的织构组分;换向轧制促进(0001)的强基面织构向ND-TD面和RD-TD面发生漫射,并存在一定角度的偏转,有效降低棱锥型织构强度,促进织构组分重新分配,显著改善板材的各向异性。

    Abstract:

    The influence of two cold rolling processes of unidirectional rolling and cross rolling on the microstructure, mechanical properties and texture of TC4 alloy plate was studied in this paper. The research results show that the grains of the two rolling processes are all refined. The microstructure of the unidirectional rolling still has a band structure, and the α grains elongated with rolling direction. The microstructure of the cross rolling is a uniform composition of equiaxed α grains and intercrystalline β. The plasticity of the cross rolling process is significantly better than that of the unidirectional rolling, and the strength is slightly lower than that of the unidirectional cold rolling. But the difference between the RD and TD directions of the plate is significantly reduced. The original cold-rolled plate mainly has (-12-10)<10-10> pyramid texture with strong intensity. Unidirectional cold rolling inherits the texture components of the original plate. Cross rolling promotes strong basal texture of (0001) diffuse to the ND-TD surface and the RD-TD surface, and which deflected a certain angle. The intensity of the pyramid texture is effectively decreased, which improves the anisotropy of the plate. Crossing rolling process promotes redistribution of texture components and weakens anisotropy.

    参考文献
    相似文献
    引证文献
引用本文

韩盈,余伟,董恩涛,程知松.轧制工艺对TC4合金板材织构演变及组织性能的影响[J].稀有金属材料与工程,2021,50(10):3585~3590.[Han Ying, Yu Wei, Dong Entao, Cheng Zhisong. Effect of rolling process on texture evolution, microstructure and mechanical properties of TC4 alloy plate[J]. Rare Metal Materials and Engineering,2021,50(10):3585~3590.]
DOI:10.12442/j. issn.1002-185X.20200799

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2020-10-18
  • 最后修改日期:2020-12-24
  • 录用日期:2021-02-03
  • 在线发布日期: 2021-10-28
  • 出版日期: 2021-10-25