Microstructure Evolution and Deformation Behavior of Metastable β-Titanium Alloy Ti55511 in Die Forging
Author:
Affiliation:

1.School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;2.AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China

Fund Project:

National Science and Technology Project of China (JPPT-135-GH-2-017); Fellowship of China Postdoctoral Science Foundation (2022M720399)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用电子背散射衍射法研究了模锻对亚稳态β钛合金Ti55511显微组织演变和变形行为的影响。在模锻之前,对Ti55511合金进行了多道次锻造,以优化钛合金织构导致的力学行为各向异性。结果表明,模锻后,Ti55511部件局部区域表现出不同的显微组织和织构。在所有变形区域都没有发现<100>纤维织构。动态回复再结晶发生在模锻早期承受大应变的区域,大多数局部区域形成了网篮组织。

    Abstract:

    The effect of die forging on the microstructure evolution and deformation behavior of metastable β-titanium alloy Ti55511 was investigated by electron backscatter diffraction. Before die forging, the alloy Ti55511 was subjected to multi-pass forging to optimize the microstructural heterogeneity (texture) which can cause mechanical behavior anisotropy of titanium alloys. Results show that after die forging, Ti55511 components exhibit different microstructures and textures in different local areas. No <100> fiber texture is found in all areas with different degrees of deformation. Dynamic recrystallization occurs in the area where large strain occurs during the early stage of die forging. Basket-weave microstructure forms in most local areas.

    参考文献
    相似文献
    引证文献
引用本文

谷宾,熊智豪,杨平,顾新福,颜孟奇,沙爱学.亚稳态 β 钛合金Ti55511模锻过程中显微组织演变与变形行为[J].稀有金属材料与工程,2024,53(9):2420~2429.[Gu Bin, Xiong Zhihao, Yang Ping, Gu Xinfu, Yan Mengqi, Sha Aixue. Microstructure Evolution and Deformation Behavior of Metastable β-Titanium Alloy Ti55511 in Die Forging[J]. Rare Metal Materials and Engineering,2024,53(9):2420~2429.]
DOI:10.12442/j. issn.1002-185X.20240152

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2024-03-15
  • 最后修改日期:2024-06-16
  • 录用日期:2024-06-17
  • 在线发布日期: 2024-09-12
  • 出版日期: 2024-09-04