Microstructure Evaluation and Mechanical Properties of Ti6Al4V/Inconel 718 Composites Prepared by Direct Laser Deposition
Author:
Affiliation:

No.2 Linggong Road, Ganjingzi District, Dalian City, Liaoning Province

Fund Project:

China Postdoctoral Science Foundation (No.2018T110215), National Key R & D Program of China(No. 2018YFB1107801), Science Fund for Creative Research Groups of NSFC (No. 51621064), National Natural Science Foundation of China (No. 51805070)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    Ti6Al4V和Inconel 718合金被广泛用于航空航天。但TC4或Inconel 718难以同时满足轻量化和耐高温的需求。本文采用直接激光沉积制备了不同比例Ti6Al4V / Inconel 718复合材料。分别通过X射线衍射,扫描电子显微镜和能谱仪分析相组成,微观结构和元素分布。同时,研究了显微硬度和摩擦磨损性能。研究表明:随着Inconel 718的比例增加,有Ti2Ni和Ni3Ti金属间化合物形成。Ti2Ni的形成机理为:β→α+ Ti2Ni和L→β-Ti+ Ti2Ni,且Ti2Ni金属间化合物的偏析机理为晶间偏析。随着Inconel 718含量增加,复合材料的显微硬度逐渐增加。当Inconel 718的体积分数为50%时,其平均显微硬度值为770 HV,比100% Ti6Al4V的平均显微硬度高85.5%。显微硬度增加与Ti2Ni金属间化合物的析出强化直接相关。复合材料以磨料磨损为主,并伴随着黏着磨损。随着Inconel 718的增加,黏着磨损减弱。当Inconel 718的体积分数达到达到50%时,磨损量仅为100% Ti6Al4V的36.9%。

    Abstract:

    Ti6Al4V and Inconel 718 alloys are both extensively used in the aerospace industry. However, TC4 or Inconel 718 is difficult to meet the demand of both light weight and high temperature resistance. In this paper, the composites of different Ti6Al4V/Inconel 718 ratios were prepared by direct laser deposition. The phase, microstructure and element distribution were analyzed by X-ray Diffraction, scanning electron microscope and energy dispersive spectrometer, respectively. The microhardness, friction and wear properties were also investigated. With Inconel 718 increasing, Ti2Ni and Ni3Ti intermetallic compound were formed. The forming mechanism of Ti2Ni is: β→α+Ti2Ni and L→β-Ti+Ti2Ni, and the segregation mechanism of Ti2Ni intermetallic compound was intergranular segregation. As the doping of Inconel 718 increased, the microhardness of the composites increased gradually. When the volume fraction of Inconel 718 was 50%, the average microhardness value was 770 HV, which was 85.5% higher than that of 100% Ti6Al4V. The reason for the increase of microhardness was directly related to Ti2Ni intermetallic compound precipitation strengthening. Wear experiments showed that the composites were dominated by abrasive wear and accompanied by adhesive wear. As Inconel 718 increased, the adhesion was weakened, and when Inconel 718 reached 50% volume fraction, the wear volume was just 36.9% of that of 100% Ti6Al4V.

    参考文献
    相似文献
    引证文献
引用本文

吴东江,元世军,余超,何爱迪,马广义,牛方勇,卢凡.直接激光沉积Ti6Al4V/Inconel 718复合材料微观组织与力学性能分析[J].稀有金属材料与工程,2021,50(1):78~84.[Dalian University of Technology, Yuan shijun, Yu Chao, He aidi, Ma Guangyi, Niu Fangyong, Lu Fan. Microstructure Evaluation and Mechanical Properties of Ti6Al4V/Inconel 718 Composites Prepared by Direct Laser Deposition[J]. Rare Metal Materials and Engineering,2021,50(1):78~84.]
DOI:10.12442/j. issn.1002-185X. E20190111

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-12-05
  • 最后修改日期:2020-02-13
  • 录用日期:2020-02-20
  • 在线发布日期: 2021-02-05
  • 出版日期: