转速对铝/镁搅拌摩擦焊接头金属间化合物及低熔点共晶的影响
作者:
作者单位:

1.西北工业大学 凝固技术国家重点实验室,陕西 西安 710072;2.南昌航空大学 轻合金加工科学与技术国防重点学科实验室,江西 南昌 330063

作者简介:

通讯作者:

中图分类号:

基金项目:

国家自然科学基金项目(面上项目,重点项目,重大项目)


Effect of Rotational Speed on Intermetallic Compounds and Low Melting Point Eutectic of Al/Mg Friction Stir Welded Joints
Author:
Affiliation:

1.State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China;2.National Defense Key Discipline Laboratory of Light Alloy Processing Science and Technology, Nanchang Hangkong University, Nanchang 330063, China

Fund Project:

National Natural Science Foundation of China (51874179, 52005240)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    研究了转速对铝/镁搅拌摩擦焊接头金属间化合物和低熔点共晶的影响,并用电子背散射衍射表征了铝侧和镁侧界面微观结构。结果表明,当采用375 r/min的低转速时,镁侧界面上部出现由Mg固溶体和Al12Mg17相组成的共晶层,平均厚度为38.83 μm。在镁侧界面上部还发现一层厚度为12.3 μm的连续柱状Al3Mg2层,垂直于Al3Mg2层与共晶层的边界。在镁侧界面的中部和底部,只有Al3Mg2层和Al12Mg17层,其厚度沿厚度方向从上到下依次减小。此外,铝侧和镁侧界面的Al3Mg2层具有较高的平均晶粒取向差,这为铝和镁原子间的扩散提供了一条途径。当转速为600 r/min时,Mg固溶体与Al12Mg17相组成的共晶层沿厚度方向分布在镁侧界面上,共晶层厚度较低转速(375 r/min)时显著增加。镁侧界面上部的Al3Mg2层和共晶层的平均厚度分别为32.89和68.92 μm。最后,由转速引起的应变速率对金属间化合物的生长起着重要作用。

    Abstract:

    The effects of rotational speed on the intermetallic compounds and low melting point eutectic of Al/Mg friction stir welded joints were investigated. The interfacial microstructures of both Al and Mg sides were characterized by electron backscatter diffraction. The results show that when the low rotational speed of 375 r/min is used, the eutectic layer (Mg+Al12Mg17), with an average thickness of 38.83 μm, appears at the upper of the Mg side interface. A continuous columnar Al3Mg2 layer with a thickness of 12.3 μm, perpendicular to the boundary between the Al3Mg2 layer and eutectic layer, is also found at the upper of the Mg side interface. At the middle and bottom of the Mg side interface, there are merely Al3Mg2 layer and Al12Mg17 layer, the thickness of which decreases sequentially from the upper to the bottom along the thickness direction. In addition, the Al3Mg2 layer with high kernel average misorientation at the Al and Mg side interface provides a path for the diffusion of Al and Mg atoms. When the high rotational speed of 600 r/min is used, the eutectic layer composed of Mg solid solution and Al12Mg17 phase is distributed across the Mg side interface along the thickness direction, and the thickness of the eutectic layer increases significantly compared with that at the low rotational speed of 375 r/min. The average thickness of the Al3Mg2 layer and eutectic layer on the upper of the Mg side interface is 32.89 and 68.92 μm, respectively. Finally, the strain rate caused by rotational speed plays an important role in the growth of intermetallic compounds.

    参考文献
    相似文献
    引证文献
引用本文

徐洋,柯黎明,毛育青,陈宜.转速对铝/镁搅拌摩擦焊接头金属间化合物及低熔点共晶的影响[J].稀有金属材料与工程,2021,50(12):4209~4217.[Xu Yang, Ke Liming, Mao Yuqing, Chen Yi. Effect of Rotational Speed on Intermetallic Compounds and Low Melting Point Eutectic of Al/Mg Friction Stir Welded Joints[J]. Rare Metal Materials and Engineering,2021,50(12):4209~4217.]
DOI:10.12442/j. issn.1002-185X. E20200047

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2020-09-21
  • 最后修改日期:2020-10-23
  • 录用日期:2020-11-25
  • 在线发布日期: 2021-12-30
  • 出版日期: 2021-12-24