MoS2/CoS2 binary composites for supercapacitor electrode materials
Author:
Affiliation:

1.State Key Laboratory of New Ceramics and Fine Processing,School of Materials Science and Engineering,Tsinghua University;2.PR China;3.Aerospace Institute of Advanced Materials Processing Technology;4.PR ChinaState Key Lab of New

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用“一步水热法”合成了不同原料配比的MoS2/CoS2二元复合材料,并研究了其用作超级电容器电极材料的电化学性能。研究结果显示,当原料中Mo: Co(摩尔比)= 2:1时(简称M2C1),该复合材料具有最优的循环稳定性能和最高的比电容,2 mV/s 扫描速度下,比电容为549 F/g或1 A/g电流密度下,比电容为434 F/g。微观结构表明,该复合材料主要由八面体形状的CoS2和花状的MoS2组成。综合分析可知,优异的电化学性能主要归因于两种组元材料的协同效应、大的比表面积以及可调控的组分含量等因素。

    Abstract:

    A facile one-step hydrothermal process was used to prepare MoS2/CoS2 binary composites with different raw material ratio as electrode material for supercapacitors. Results of electrochemical performances show that MoS2/CoS2 binary composites exhibit competitive specific capacitance (549 F/g at 2 mV/s or 434 F/g at 1 A/g) and excellent cycling stability as the molar ratio of Mo: Co=2:1 in raw material. And microstructure and morphology analyses reveal that the MoS2/CoS2 binary composites were composed of octahedron-shaped CoS2 and flower-liked MoS2. Above all, due to the coupling two species, large surface areas and tunable compositions, the obtained MoS2/CoS2 binary composites electrodes possess the best electrochemical properties.

    参考文献
    相似文献
    引证文献
引用本文

李海燕,韩耀,陈林辉,汪长安.用于超级电容器电极材料的MoS2/CoS2二元复合材料[J].稀有金属材料与工程,2020,49(2):605~610.[Haiyan Li, Yao Han, Linhui Chen, Chang-An Wang. MoS2/CoS2 binary composites for supercapacitor electrode materials[J]. Rare Metal Materials and Engineering,2020,49(2):605~610.]
DOI:10.12442/j. issn.1002-185X. QH20190040

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-03-19
  • 最后修改日期:2019-05-09
  • 录用日期:2019-10-23
  • 在线发布日期: 2020-03-12
  • 出版日期: