Magnetic Entropy Change of Gd60Co26Al14 Bulk Metallic Glass
DOI:
Author:
Affiliation:
Clc Number:
Fund Project:
Article
|
Figures
|
Metrics
|
Reference
|
Related
|
Cited by
|
Materials
|
Comments
Abstract:
Bulk metallic glassy (BMG) alloys Gd60Co26Al14 were prepared by a copper-mold casting method. Their structure and thermomagnetic properties were studied by DSC, XRD and SQUID. XRD analysis shows that the as-cast Gd60Co26Al14 cylinder was fully amorphous structure in 3 mm diameter. The DSC reveals that Gd60Co26Al14 BMG had a distinct glass transition temperature at 571 K and two crystallization temperatures at 602 K and 642 K, respectively. SQUID measurements indicate that the Gd60Co26Al14 BMG had two Curie temperatures occurring at 82 K and 128 K, respectively. The entropy change was 7 J·(kg·K)-1 at 82 K in 5 T magnetic field
Reference
Related
Cited by
Get Citation
[Zhang Xiaoyan, Fu Hao, Zu Xiaotao, Yu Huajun. Magnetic Entropy Change of Gd60Co26Al14 Bulk Metallic Glass[J]. Rare Metal Materials and Engineering,2009,38(3):431~433.] DOI:[doi]