Microstructure and damping of Mg97Zn1Y2 with or without solid solution treatment
Affiliation:

School of Mechanical and Electrical Engineering,East China Jiaotong University,School of Mechanical and Electrical Engineering,East China Jiaotong University

  • Article
  • | |
  • Metrics
  • |
  • Reference [12]
  • |
  • Related [20]
  • | | |
  • Comments
    Abstract:

    The microstructure of as-cast Mg97Zn1Y2 with or without solid solution treatment was analysised by OM and SEM.Meanwhile, phase analysis was carried out by EDS and XRD. After solid solution treatment, LPSO phase grow up,turning into continuous distribution in Mg97Zn1Y2.Through damping testing, it was found that the damping capacity of Mg97Zn1Y2 was declined after solid solution treatment.The damping-temperture specturm of the as-cast Mg97Zn1Y2 with or without solid solution treatment was also analysised. There are two internal friction peaks:damping peak P1 located between 150 ℃ and 250 ℃ and the peak is very wide, which is caused by the dislocation mechanism.Meanwhile, the damping peak P2 is near the 350-500 ℃, which is preliminary considered as grain boundary internal friction peak.

    Reference
    [1] 王敬丰,赵亮,胡耀波等.材料导报[J],2008,50(3):103
    [2] Luo Z P,Zhang S Q,Tang Y L,et al.J Alloys Compd[J],1994,209(1-2):275
    [3] Kawamura Y,Hayashik,Inoue A,et al,Meterials Transactions[J],2001,42(7):1172
    [4] 冯娟妮,郭学锋,徐春杰,张忠明.中国稀土学报[J],2006,24(1):86
    [5] 石德珂,朱维斗.材料物理[M].北京:机械工业出版社,2006:271
    [6] Granato A, Luckek.Journal of Applied Physics[J],1956,27(6):583
    [7] Granato A, Luckek.Journal of Applied Physics[J],1956,27(7):789
    [8]黎文献 镁及镁合金[M].长沙;中南大学出版社,2005:91
    [9]王敬丰,凌闯等.兵器材料科学与工程 [J],2009,32(3):90
    [10] 万迪庆,杨根仓,王锦程.铸造技术[J],2009,30(7):904
    [11]Diqing Wan,Jingcheng Wang et al.,Acta.Metall.Sin[J],2009,22(1):1
    [12] 葛庭遂 固体内耗理论基础[M].北京;科学出版社,2000:238
    Cited by
    Comments
    Comments
    分享到微博
    Submit
Get Citation

[Wan Diqing, Li zhumin. Microstructure and damping of Mg97Zn1Y2 with or without solid solution treatment[J]. Rare Metal Materials and Engineering,2016,45(5):1245~1248.]
DOI:[doi]

Copy
Article Metrics
  • Abstract:1634
  • PDF: 1619
  • HTML: 149
  • Cited by: 0
History
  • Received:January 30,2015
  • Revised:May 05,2015
  • Adopted:June 11,2015
  • Online: June 02,2016