Temperature Sensitivity of Fatigue Crack Growth Rate for GH4720Li Alloy

Home > Archive>Volume 46, Issue 10, 2017 >2915-2921

Temperature Sensitivity of Fatigue Crack Growth Rate for GH4720Li Alloy
DOI:
                        
Author:
                        
Affiliation:School of Materials Science and Engineering,University of Science and Technology Beijing,School of Materials Science and Engineering,University of Science and Technology Beijing,School of Materials Science and Engineering,University of Science and Technology Beijing,School of Materials Science and Engineering,University of Science and Technology Beijing,School of Materials Science and Engineering,University of Science and Technology Beijing,High Temperature Materials Research Institute,Central and Steel Research Institute
Clc Number:
Fund Project:

Article

Figures

Metrics

Reference

Cited by

Materials

Comments

Abstract:

The fatigue crack growth rate of difficult-to-deform superalloy GH4720Li are investigated at 650℃, 700℃, 750℃and 800℃. The analysis of temperature effect on fatigue crack growth rate under pure fatigue and fatigue with 90s dwell. The result shows that the fatigue crack growth rate(FCGR) and increasing rate increased as the temperature increased. FCGR increase rapidly at 800℃. Temperature changes the model of the fatigue crack propagation, the fracture mode is the mix of transgranular and intergranular at 650℃, the fracture mode is predominantly inergranular at 700~800℃. The crack growth rate increased significantly with increasing the holding time. The higher test temperature is, the greater effect of dwell time on crack growth rate.

Reference

Cited by

Get Citation

[Nai Qiliang, Dong Jianxin, Zhang Maicang, Zheng Lei, Yao Zhihao, Qu Jinglong. Temperature Sensitivity of Fatigue Crack Growth Rate for GH4720Li Alloy[J]. Rare Metal Materials and Engineering,2017,46(10):2915~2921.]
DOI：[doi]

Copy

Article Metrics

Abstract:
PDF:
HTML:
Cited by:

History

Received:June 14,2015
Revised:February 02,2016
Adopted:February 24,2016
Online: December 01,2017
Published:

Home

Introduction

Editorial Board

Submission Guideline

Contact Us

中文

Get Citation

Article Metrics

History