Behavior of small and long fatigue crack propagration of TiAl alloy at elevated temperature
Author:
Affiliation:

Aviation Key Laboratory of Science and Technology on Materials Testing and Evaluation,Beijing Key Laboratory of Aeronautical Materials Testing and Evaluation,Beijing Institute of Aeronautical Matarials

Clc Number:

TG146.2

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    Three-dimensional small crack propagation behavior of deforming TiAl alloy at 650℃ is studied by in-situ observation fatigue testing, and then long crack propagation behavior of the alloy in temperature range from 650℃ to 800℃ is studied by fatigue crack propagation tests. It shows that, the three-dimensional small cracks can still grow even though in the stress intensity factor region that below the long crack propagation threshold value, furthermore, the growth rates of small cracks are higher than long cracks in this region; The sample edge straight horizontal manufacturing nick is one of the main positions of three-dimensional small crack initiation of the alloy. Small cracks merge at the position of bends that occur during the fatigue testing. The fatigue life of the alloy is not sensitive to irregular strip manufacturing defects on the surface of the sample; The steady propagation rates of long fatigue cracks of the alloy are not sensitive to temperature changes in temperature range from 650℃ to 800℃. All the long crack propagation processes exhibit the cleavage fracture. Crack propagation threshold values are related to ductile-brittle transition temperature, the temperatures below the ductile-brittle transition temperature have lower threshold values.

    Reference
    Related
    Cited by
Get Citation

[Jiao Zehui, Yu Huichen, Dong Chengli, Lu Yuan, Gao Fan. Behavior of small and long fatigue crack propagration of TiAl alloy at elevated temperature[J]. Rare Metal Materials and Engineering,2019,48(2):538~544.]
DOI:10.12442/j. issn.1002-185X.20170477

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:June 05,2017
  • Revised:September 27,2017
  • Adopted:October 12,2017
  • Online: March 15,2019
  • Published: