Solidification and segregation behavior of nickel-based superalloy GH4282
Author:
Affiliation:

1.University of Science and Technology Beijing;2.Central Iron and Steel Research Institute

Clc Number:

TG132.3;TG111.4;TG113

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    The solidification process and the segregation behavior of the elements of GH4282 superalloy were investigated by a combination of differential scanning calorimeter (DSC), microstructure observation and thermodynamic calculation. The solidification sequence and the characteristics of elements segregation were obtained. The results show that the solidification sequence of GH4282 is as follows: γ matrix, MC carbide and a small amount of boride. The solidus-liquidus temperature range determined by DSC is 1316~1367 ℃. The measured solvus temperature of MC carbide, M6C carbide and γ′ phase is 1338 ℃, 1092 ℃and 1003 ℃, respectively. Thermodynamic calculations show that C, B, Ti and Mo segregate to the interdendritic regions, while Al segregates to the dendrite cores. Cr, Fe and Co do not exhibit any significant tendency to segregate to either the interdendritic region or the dendrite core during the solidification process of GH4282 superalloy. These results about segregation behavior of the elements agree well with those observed by as-cast microstructure observation.

    Reference
    Related
    Cited by
Get Citation

[Yan Xiaofeng, Dong Jianxin, Shi Zhaoxia, Duan Chunhua. Solidification and segregation behavior of nickel-based superalloy GH4282[J]. Rare Metal Materials and Engineering,2019,48(10):3183~3189.]
DOI:10.12442/j. issn.1002-185X.20180461

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:May 07,2018
  • Revised:June 27,2018
  • Adopted:July 31,2018
  • Online: November 01,2019
  • Published: