Effect of Thermal Exposure on Microstruture and Properties of Cr-12Nb-4.4Ni Alloy
Author:
Affiliation:

Nanchang Hongkong University

Clc Number:

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    The Cr-12Nb-4.4 Ni alloy, prepared by mechanical alloying and hot pressing, was thermally exposed at 1200℃ for 30, 50 and 100 h, respectively. Then, the microstructure and properties of the thermally exposed Cr-12Nb-4.4Ni alloy were studied. The results show that the phase constituent is stable during the thermal exposure process. It consists of Cr solid solution (Crss) and NbCr2, and Ni is mainly presented in NbCr2. Grain size of Crss increases with the thermal exposure time, while grain size of NbCr2 particle has no obvious change. The NbCr2 structure becomes loose due to the replacement of Cr by Ni. The increase of compressive stress in the phase interface of Cr/NbCr2 promotes the emergence of dislocations in Cr matrix and the increase of stacking fault/ twinning fault in NbCr2 particles. With the thermal exposure time, the compressive strength, yield strength and plastic strain of the Cr-12Nb-4.4 Ni alloy decrease slightly while the alloy still remains relatively high room temperature strength and good plastic during the thermal exposure process. After thermal exposure for 100h, the compressive strength, yield strength and plastic strain are 2170MPa, 1406MPa and 9.5%, respectively. The Cr-12Nb-4.4 Ni alloy can keep good fracture toughness after thermal exposure for 100h.

    Reference
    Related
    Cited by
Get Citation

[Deng Liping, Lu Shiqiang, Tang Binbing. Effect of Thermal Exposure on Microstruture and Properties of Cr-12Nb-4.4Ni Alloy[J]. Rare Metal Materials and Engineering,2019,48(12):4068~4073.]
DOI:10.12442/j. issn.1002-185X.20180953

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:September 13,2018
  • Revised:October 20,2018
  • Adopted:October 24,2018
  • Online: January 07,2020
  • Published: