Effect of welding temperature and holding time on microstructure and properties of Ni-14Cr-10P-xTi brazing filler C/C composites
Author:
Affiliation:

Powder Metallurgy Research Institute, Central South University

Clc Number:

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    Ni-14Cr-10P metal powder was prepared by vacuum melting and inert gas atomization, and then Ti powder and polymer paste were added and stirred at high speed to prepare Ni-14Cr-10P-xTi paste active solder. The C/C composites were welded in the vacuum brazing furnace with the prepared active solder paste, and then the welded joint shear strength was tested. The microstructure and mechanical properties of the joints were investigated by SEM, EDS and XRD. The results show that the strength of the welded joint decreases with the increase of welding temperature and the holding time;The addition of Ti accelerates the decrease of welding strength with temperature and holding time. Combined with the microstructure, the reason why the welding strength decreases with the increase of temperature and holding time after the addition of Ti element is analyzed.

    Reference
    Related
    Cited by
Get Citation

[Yi ZhenHua, Ran LiPing, Yi MaoZhong. Effect of welding temperature and holding time on microstructure and properties of Ni-14Cr-10P-xTi brazing filler C/C composites[J]. Rare Metal Materials and Engineering,2020,49(1):361~369.]
DOI:10.12442/j. issn.1002-185X.20181272

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:December 21,2018
  • Revised:March 25,2019
  • Adopted:April 10,2019
  • Online: February 16,2020
  • Published: