Microstructure and Mechanical Properties of Ultrafine-grained CoCrFeMnNiGd0.15 High-entropy Alloy Fabricated by Powder Metallurgy
Author:
Affiliation:

Clc Number:

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    The Ultrafine-grained CoCrFeMnNiGd0.15 high-entropy alloy (HEA) was prepared by mechanical alloying (MA) and spark plasma sintering (SPS). The microstructure and mechanical properties of CoCrFeMnNi Gd0.15 high-entropy alloy was investigated. It was found that the sintered CoCrFeMnNiGd0.15 alloy showed a multi-phase microstructure including the FCC matrix, a rare earth oxide (Gd2O3) and a tetragonal phase rich in Gd, Ni and Mn element. As the sintering temperature increased, the content and size of the precipitated phase increased continuously, the compressive yield strength of the alloy decreased while the plasticity showed the opposite trend. The sintered alloy achieved the best comprehensive mechanical properties at the sintering temperature of 900 °C, with a compressive yield strength of 1662 MPa, compressive strength of 2518 MPa, plastic strain of 30.6% and Vickers hardness of 458 Hv. With the increase of temperature, the fracture morphology of compressive specimens consisted of fine equiaxed dimples, the diameter and depth of the dimples increased continuously and some tearing ridges were observed.

    Reference
    Related
    Cited by
Get Citation

[Long Yan, Zhang Weihua, Peng Liang, Li Guiqi, Peng Haiyan. Microstructure and Mechanical Properties of Ultrafine-grained CoCrFeMnNiGd0.15 High-entropy Alloy Fabricated by Powder Metallurgy[J]. Rare Metal Materials and Engineering,2020,49(11):3841~3846.]
DOI:10.12442/j. issn.1002-185X.20190954

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:November 14,2019
  • Revised:December 13,2019
  • Adopted:January 03,2020
  • Online: December 09,2020
  • Published: