The Constitutive Relation and Secondary Recrystallization Maps of the TC18 Titanium Alloy during the Hot Deformation
Author:
Affiliation:

Clc Number:

Fund Project:

Scientific and technological innovation projects of Hunan Province, China (No. 2017GK2292); Innovation and Entrepreneurship training Project for Undergraduate in Hunan Province in 2019 (GS20191053328); State Key Laboratory of Powder Metallurgy, Central South University (No. 20181106).

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    The constitutive equation and the secondary recrystallization maps, which reflect the flow stress characteristics and microstructure-deformation relationship of the material respectively, are the key data for the TC18 titanium alloy during the hot deformation. The hot compression deformation was taken on a Gleeble-3800 with the conditions that the deformation temperatures were 790℃~900℃, the strain rates were 0.01s-1~10s-1 and the strains were 0.1~0.5. By fitting the 6th polynomials of ε and α, n, Q, lnA in the Arrhenius formula respectively, TC18 titanium alloy’s constitutive equation of hot compression was established,the predicted values of flow stress of the hot compression are in a good agreement with the measured values; the secondary recrystallization maps of each strain rate were drawn by observing the microstructure and measuring α grains’ sizes.

    Reference
    Related
    Cited by
Get Citation

[leiyu, xunianao, zhangchenjie, zhaoyao, yangyang, anzehao. The Constitutive Relation and Secondary Recrystallization Maps of the TC18 Titanium Alloy during the Hot Deformation[J]. Rare Metal Materials and Engineering,2020,49(12):4192~4198.]
DOI:10.12442/j. issn.1002-185X.20191100

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:December 28,2019
  • Revised:February 20,2020
  • Adopted:March 05,2020
  • Online: January 13,2021
  • Published: