Effect of heat treatment on the microstructure and mechanical propertiesof P/M Inconel 718 superalloy
Author:
Affiliation:

1.State Key Laboratory of Solidification Processing,Northwestern Polytechnical University,Xi’an;2.Sino-Euro Materials Technologies of Xi’an Co,Ltd,Xi’an

Clc Number:

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    Powder metallurgy (P/M) Inconel 718 superalloy was processed through hot isostatic pressing (HIP) route by SS-PREP powder. Effect of heat treatment on the microstructure and mechanical properties of superalloy was research. The results indicated that the distribution of size of Inconel 718 superalloy SS-PREP powder uniformity, with the fine degree of sphericity. HIP at 1210℃/120MPa for 4h, average size of grain was 50μm, tensile strength at room temperature was 1260MPa. Tensile strength at room temperature achieve to 1404MPa through solution treatment at different temperatures and two-step ageing treatment, and Tensile strength at 650℃ achieve to 1150MPa. Optimum properties of Inconel 718 superalloy appears when solution treatment at 980℃.

    Reference
    Related
    Cited by
Get Citation

[Han Zhiyu, Zhang Pingxiang, Song Jiaming, Wang Qingxiang, Liang Shujin, Tang Bin, Lai Yunjin. Effect of heat treatment on the microstructure and mechanical propertiesof P/M Inconel 718 superalloy[J]. Rare Metal Materials and Engineering,2021,50(2):693~698.]
DOI:10.12442/j. issn.1002-185X.20200421

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:June 15,2020
  • Revised:August 10,2020
  • Adopted:August 28,2020
  • Online: March 09,2021
  • Published: